LNP™STAT-KON™ Compound LCP 9X08403C 塑料物性表
Also known as:LNP™ Stat-kon™ Compound 9X08403C
Product reorder name:9X08403C
LNP* Stat-Kon* 9X08403C is a compound based on Liquid Crystal Polymer (LCP) resin containing Carbon Fiber. Added features include: Clean Compounding System, High Temperature, inherently Flame Retardant and very good barrier against water and oxygen.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,5mm/min | 1560 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,5mm/min | 2.7 | % | ASTM D 638 |
Tensile Modulus,5mm/min | 150900 | kgf/cm² | ASTM D 638 |
Flexural Stress | 540 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3mm/min,50mm span | 146800 | kgf/cm² | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 84 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 8 | cm-kgf/cm | ASTM D 256 |
THERMAL | Value | Unit | Standard |
HDT,1.82 MPa,3.2mm,unannealed | 280 | ℃ | ASTM D 648 |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.46 | - | ASTM D 792 |
Density | 1.46 | g/cm³ | ASTM D 792 |
Mold Shrinkage,flow(5) | 0.2 | % | SABIC Method |
Mold Shrinkage,xflow(5) | 0.52 | % | SABIC Method |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 1.E+05-1.E+09 | Ohm-cm | ASTM D 257 |
Surface Resistivity | 1.E+05-1.E+09 | Ohm | ASTM D 257 |
Source GMD,last updated:2011/09/21 |