ZENITE 6130L | LCP | Glass Reinforced
Description
Zenite® 6130L is a lubricated 30% glass reinforced LCP resin. It is well suited for use in automotive, electrical/electronic, telecommunications, and aerospace industries.
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
Phys |
Density |
1620 |
kg/m³ |
ISO 1183 |
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
Tensile modulus (1mm/min) |
13000 |
MPa |
ISO 527-2/1A |
Tensile stress at break (5mm/min) |
130 |
MPa |
ISO 527-2/1A |
Tensile strain at break (5mm/min) |
1.8 |
% |
ISO 527-2/1A |
Flexural modulus (23℃) |
12000 |
MPa |
ISO 178 |
Charpy impact strength @ 23℃ |
35 |
kJ/m² |
ISO 179/1eU |
Charpy notched impact strength @ 23℃ |
35 |
kJ/m² |
ISO 179/1eA |
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
Melting temperature (10℃/min) |
335 |
℃ |
ISO 11357-1,-2,-3 |
DTUL @ 1.8 MPa |
265 |
℃ |
ISO 75-1/-2 |
Coeff.of linear therm. expansion (parallel) |
0.03 |
E-4/℃ |
ISO 11359-2 |
Coeff.of linear therm. expansion (normal) |
0.7 |
E-4/℃ |
ISO 11359-2 |
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
thickness tested (1.6) |
1.5 |
mm |
UL94 |
UL recognition (1.6) |
UL |
- |
UL94 |
Flammability at thickness h |
V-0 |
class |
UL94 |
thickness tested (h) |
0.38 |
mm |
UL94 |
UL recognition (h) |
UL |
- |
UL94 |
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
Dissipation factor - 1 MHz |
310 |
E-4 |
IEC 60250 |
Volume resistivity |
>1E14 |
Ohm*m |
IEC 60093 |
Surface resistivity |
>1E16 |
Ohm |
IEC 60093 |
Electric strength |
36 |
kV/mm |
IEC 60243-1 |
Comparative tracking index CTI |
200 |
- |
IEC 60112 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
Drying time (h):3
Drying temperature (℃):150-150