- 产 品：LCP E115i 含15%玻璃纤维增强
- 产 地：泰科纳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
VECTRA® LKX1387 BK210P BLACK
VECTRA E115i | LCP | Glass Reinforced
Description
VECTRA LCP E115i 15% glass reinforced
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant.
FDA compliant
UL-Listing V-0 black at 0.75mm thickness per UL 94 flame testing.
UL = Underwriters Laboratories (USA)
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1460 | kg/m³ | ISO 1183 |
| Mold shrinkage - parallel | -0.2 | % | ISO 294-4 | |
| Mold shrinkage - normal | 0.5 | % | ISO 294-4 | |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus (1mm/min) | 14000 | MPa | ISO 527-2/1A | |
| Tensile stress at break (5mm/min) | 175 | MPa | ISO 527-2/1A | |
| Tensile strain at break (5mm/min) | 2.3 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 14000 | MPa | ISO 178 | |
| Flexural strength (23℃) | 210 | MPa | ISO 178 | |
| Unnotched impact str (Izod) @ 23℃ | 101 | kJ/m² | ISO 180/1U | |
| Notched impact strength (Izod) @ 23℃ | 40 | kJ/m² | ISO 180/1A | |
| Rockwell hardness | 43 | M-Scale | ISO 2039-2 | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 336 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 252 | ℃ | ISO 75-1/-2 | |
| DTUL @ 0.45 MPa | 298 | ℃ | ISO 75-1/-2 | |
| Vicat softening temperature B50 (50℃/h 50N) | 202 | ℃ | ISO 306 | |
| Flammability at thickness h | V-0 | class | UL94 | |
| thickness tested (h) | 0.75 | mm | UL94 | |
| UL recognition (h) | UL | - | UL94 | |
| Elec | Electrical properties | Value | Unit | Test Standard |
| Volume resistivity | >1E14 | Ohm*m | IEC 60093 | |
| Surface resistivity | >1E15 | Ohm | IEC 60093 | |
| Electric strength | 33 | kV/mm | IEC 60243-1 | |
| SpecProd | Test specimen production | Value | Unit | Test Standard |
| Injection molding melt temperature | 340 | ℃ | ISO 294 | |
| Injection molding mold temperature | 100 | ℃ | ISO 294 | |
| Injection molding flow front velocity | 150 | mm/s | ISO 294 | |
| Injection molding hold pressure | 69 | MPa | ISO 294 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 40℃. The time between drying and processing should be as short as possible.
For subsequent storage of the material in the dryer until processed the temperature does not need to be lowered for grades A, B, C, D and V (<= 24 h).
Drying time (h):6
Drying temperature (℃):150-150