- 产 品：LCP E130G 含30%玻璃纤维填充
- 产 地：泰科纳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
VECTRA® E130G VF2201 NATURAL
VECTRA E130G | LCP | Glass Reinforced
Description
VECTRA LCP E130G 30% glass fiber filled / low injection pressure
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
UL-Listing V-0 in natural and black at 0.75mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electricals 130℃, mechanicals 130℃.
UL = Underwriters Laboratories (USA)
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1610 | kg/m³ | ISO 1183 |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus (1mm/min) | 12000 | MPa | ISO 527-2/1A | |
| Tensile stress at break (5mm/min) | 140 | MPa | ISO 527-2/1A | |
| Flexural modulus (23℃) | 12000 | MPa | ISO 178 | |
| Flexural strength (23℃) | 170 | MPa | ISO 178 | |
| Notched impact strength (Izod) @ 23℃ | 25 | kJ/m² | ISO 180/1A | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 335 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 245 | ℃ | ISO 75-1/-2 | |
| DTUL @ 0.45 MPa | 273 | ℃ | ISO 75-1/-2 | |
| Coeff.of linear therm. expansion (parallel) | 0.05 | E-4/℃ | ISO 11359-2 | |
| Coeff.of linear therm. expansion (normal) | 0.67 | E-4/℃ | ISO 11359-2 | |
| Flammability at thickness h | V-0 | class | UL94 | |
| thickness tested (h) | 0.75 | mm | UL94 | |
| Elec | Electrical properties | Value | Unit | Test Standard |
| Volume resistivity | >1E13 | Ohm*m | IEC 60093 | |
| Surface resistivity | >1E14 | Ohm | IEC 60093 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 40℃. The time between drying and processing should be as short as possible.
Drying time (h):4
Drying temperature (℃):150-170