- 产 品：LCP E463i 含40玻纤/矿物填充,高耐热
- 产 地：泰科纳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
VECTRA® E463I VF3001 NATURAL
VECTRA® E463ID-2 VD3005 BLACK
VECTRA® E463ID-3 VD3006 BLACK
VECTRA E463i | LCP | Mineral / Glass Reinforced
Description
40% glass/mineral filled exellent flow, low warpage, high heat resistance.
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
UL-Listing V-0 all colors at 1.5mm thickness per UL 94 flame testing.
Relative-Temperature-Index (RTI) according to UL 746B: electricals 130℃, mechanicals 130℃.
UL = Underwriters Laboratories (USA)
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1720 | kg/m³ | ISO 1183 |
| Mold shrinkage - parallel | 0.05 | % | ISO 294-4 | |
| Mold shrinkage - normal | 0.38 | % | ISO 294-4 | |
| Water absorption (23℃-sat) | 0.02 | % | ISO 62 | |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus (1mm/min) | 10000 | MPa | ISO 527-2/1A | |
| Tensile stress at break (50mm/min) | 110 | MPa | ISO 527-2/1A | |
| Tensile strain at break (50mm/min) | 3 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 10600 | MPa | ISO 178 | |
| Flexural strength (23℃) | 130 | MPa | ISO 178 | |
| Flexural strain @ break | 3.1 | % | ISO 178 | |
| Compressive stress @ 1% strain | 53 | MPa | ISO 604 | |
| Charpy impact strength @ 23℃ | 30 | kJ/m² | ISO 179/1eU | |
| Charpy notched impact strength @ 23℃ | 5 | kJ/m² | ISO 179/1eA | |
| Unnotched impact str (Izod) @ 23℃ | 30 | kJ/m² | ISO 180/1U | |
| Notched impact strength (Izod) @ 23℃ | 5 | kJ/m² | ISO 180/1A | |
| Compressive modulus | 7700 | MPa | ISO 604 | |
| Rockwell hardness | 44 | M-Scale | ISO 2039-2 | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 335 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 235 | ℃ | ISO 75-1/-2 | |
| DTUL @ 0.45 MPa | 270 | ℃ | ISO 75-1/-2 | |
| Vicat softening temperature B50 (50℃/h 50N) | 185 | ℃ | ISO 306 | |
| Coeff.of linear therm. expansion (parallel) | 0.1 | E-4/℃ | ISO 11359-2 | |
| Coeff.of linear therm. expansion (normal) | 0.43 | E-4/℃ | ISO 11359-2 | |
| Elec | Electrical properties | Value | Unit | Test Standard |
| Relative permittivity - 1 MHz | 3.9 | - | IEC 60250 | |
| Dissipation factor - 1 MHz | 35 | E-4 | IEC 60250 | |
| Volume resistivity | 1.00E+14 | Ohm*m | IEC 60093 | |
| Surface resistivity | 1.00E+16 | Ohm | IEC 60093 | |
| Electric strength | 59 | kV/mm | IEC 60243-1 | |
| Comparative tracking index CTI | 150 | - | IEC 60112 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 40℃. The time between drying and processing should be as short as possible.
For subsequent storage of the material in the dryer until processed the temperature does not need to be lowered for grades A, B, C, D and V (<= 24 h).
Drying time (h):6
Drying temperature (℃):150 - 170