VECTRA® E488I VC3052 GRAY
VECTRA® E488I VF3001 NATURAL
VECTRA® E488ID-2 BLACK
VECTRA E488i | LCP | Specialty
Description
VECTRA LCP E488i Ultra low warp
ISO Data | Physical properties | Value | Unit | Test Standard |
Phys | Density | 1770 | kg/m³ | ISO 1183 |
Mold shrinkage - parallel | 0.14 | % | ISO 294-4 | |
Mold shrinkage - normal | 0.43 | % | ISO 294-4 | |
Water absorption (23℃-sat) | 0.005 | % | ISO 62 | |
Mech | Mechanical properties | Value | Unit | Test Standard |
Tensile modulus (1mm/min) | 13000 | MPa | ISO 527-2/1A | |
Tensile stress at break (5mm/min) | 110 | MPa | ISO 527-2/1A | |
Tensile strain at break (5mm/min) | 1.5 | % | ISO 527-2/1A | |
Flexural modulus (23℃) | 13000 | MPa | ISO 178 | |
Flexural strength (23℃) | 160 | MPa | ISO 178 | |
Flexural strain @ break | 1.8 | % | ISO 178 | |
Charpy impact strength @ 23℃ | 29 | kJ/m² | ISO 179/1eU | |
Charpy notched impact strength @ 23℃ | 18 | kJ/m² | ISO 179/1eA | |
Unnotched impact str (Izod) @ 23℃ | 28 | kJ/m² | ISO 180/1U | |
Notched impact strength (Izod) @ 23℃ | 9 | kJ/m² | ISO 180/1A | |
Compressive modulus | 11000 | MPa | ISO 604 | |
Rockwell hardness | 54 | M-Scale | ISO 2039-2 | |
Therm | Thermal properties | Value | Unit | Test Standard |
Melting temperature (10℃/min) | 335 | ℃ | ISO 11357-1,-2,-3 | |
DTUL @ 1.8 MPa | 260 | ℃ | ISO 75-1/-2 | |
Vicat softening temperature B50 (50℃/h 50N) | 200 | ℃ | ISO 306 | |
Coeff.of linear therm. expansion (parallel) | 0.08 | E-4/℃ | ISO 11359-2 | |
Coeff.of linear therm. expansion (normal) | 0.42 | E-4/℃ | ISO 11359-2 | |
Flammability at thickness h | V-0 | class | UL94 | |
thickness tested (h) | 0.15 | mm | UL94 | |
Elec | Electrical properties | Value | Unit | Test Standard |
Relative permittivity - 1 MHz | 4.24 | - | IEC 60250 | |
Dissipation factor - 1 MHz | 450 | E-4 | IEC 60250 | |
Volume resistivity | 1.00E+14 | Ohm*m | IEC 60093 | |
Surface resistivity | 1.00E+17 | Ohm | IEC 60093 | |
Electric strength | 55 | kV/mm | IEC 60243-1 | |
Comparative tracking index CTI | 175 | - | IEC 60112 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
Drying time (h):6
Drying temperature (℃):150--