VECTRA FIT30 | LCP | Mineral / Glass Reinforced

Description
43% glass and mineral reinforced grade.Glass and mineral filled grade, high flow and low warpage.

Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant

ISO Data	Physical properties	Value	Unit	Test Standard
Phys	Density	1770	kg/m³	ISO 1183
Mech	Mechanical properties	Value	Unit	Test Standard
	Tensile modulus (1mm/min)	13000	MPa	ISO 527-2/1A
	Tensile stress at break (5mm/min)	130	MPa	ISO 527-2/1A
	Tensile strain at break (5mm/min)	1.7	%	ISO 527-2/1A
	Flexural modulus (23℃)	12700	MPa	ISO 178
	Flexural strength (23℃)	170	MPa	ISO 178
	Flexural strain @ break	1.9	%	ISO 178
	Charpy impact strength @ 23℃	25.5	kJ/m²	ISO 179/1eU
	Charpy notched impact strength @ 23℃	5.8	kJ/m²	ISO 179/1eA
Therm	Thermal properties	Value	Unit	Test Standard
	Melting temperature (10℃/min)	328	℃	ISO 11357-1,-2,-3
	DTUL @ 1.8 MPa	262	℃	ISO 75-1/-2
	DTUL @ 0.45 MPa	286	℃	ISO 75-1/-2
	Coeff.of linear therm. expansion (parallel)	0.09	E-4/℃	ISO 11359-2
	Coeff.of linear therm. expansion (normal)	0.38	E-4/℃	ISO 11359-2
Elec	Electrical properties	Value	Unit	Test Standard
	Volume resistivity	1.00E+14	Ohm*m	IEC 60093
	Surface resistivity	1.00E+16	Ohm	IEC 60093

Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%

VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 40℃. The time between drying and processing should be as short as possible.

For subsequent storage of the material in the dryer until processed the temperature does not need to be lowered for grades A, B, C, D and V (<= 24 h).

Drying time (h):6
Drying temperature (℃):150 - 170