- 产 品：LCP S475 超高流动,高耐热和低翘曲
- 产 地：泰科纳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
VECTRA® S475 BK010P BLACK
VECTRA® S475 VF2001 NATURAL
VECTRA® S475 VF2201 NATURAL
VECTRA S475 | LCP | Mineral / Glass Reinforced
Description
Super High Flow, High heat Resistance and Low Warp for Thin Parts.
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
UL-Listing V-0 in natural and black at 0.15mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electricals 130℃, mechanicals 130℃.
UL = Underwriters Laboratories (USA)
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1650 | kg/m³ | ISO 1183 |
| Mold shrinkage - parallel | 0.0 | % | ISO 294-4 | |
| Mold shrinkage - normal | 0.37 | % | ISO 294-4 | |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus (1mm/min) | 12300 | MPa | ISO 527-2/1A | |
| Tensile stress at break (5mm/min) | 135 | MPa | ISO 527-2/1A | |
| Tensile strain at break (5mm/min) | 1.8 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 12000 | MPa | ISO 178 | |
| Flexural strength (23℃) | 180 | MPa | ISO 178 | |
| Flexural strain @ break | 2.4 | % | ISO 178 | |
| Charpy notched impact strength @ 23℃ | 5 | kJ/m² | ISO 179/1eA | |
| Notched impact strength (Izod) @ 23℃ | 5 | kJ/m² | ISO 180/1A | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 350 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 305 | ℃ | ISO 75-1/-2 | |
| DTUL @ 8.0 MPa | 213 | ℃ | ISO 75-1/-2 | |
| Coeff.of linear therm. expansion (parallel) | 0.01 | E-4/℃ | ISO 11359-2 | |
| Coeff.of linear therm. expansion (normal) | 0.02 | E-4/℃ | ISO 11359-2 | |
| Flammability at thickness h | V-0 | class | UL94 | |
| Elec | Electrical properties | Value | Unit | Test Standard |
| Relative permittivity - 1 MHz | 3.7 | - | IEC 60250 | |
| Dissipation factor - 1 MHz | 80 | E-4 | IEC 60250 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.01%
VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 40℃. The time between drying and processing should be as short as possible.
For subsequent storage of the material in the dryer until processed the temperature does
Drying time (h):6
Drying temperature (℃):150 - 150