DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G13L NC010 is a 13% glass fiber reinforced polyamide 66 resin for injection molding.
zytel®70G13L NC010是一个13%玻璃纤维增强聚酰胺66树脂注塑。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF13
>PA66-GF13<
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
120(17.4)
3
5500(800)
4800(700)
190(27.6)
4.5
4.5
5
40
40
|
75(10.9)
13
3500(508)
2900(420)
100(14.5)
4
4
6
30
70
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
258(496)
238(460)
262(504)
0.77(0.43)
0.96(0.53)
1.58(0.88)
0.42(0.23)
0.40(0.22)
0.27(0.15)
|
|
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
2.0mm
CTI
CTI
|
IEC 60250
IEC 60093
IEC 60250
IEC 60243-1
IEC 60112
UL 746A
|
ohm m
E-4
kV/mm(V/mil)
V
V
|
3.9
3.2
1E14
130
150
25(635)
>600
>600
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Oxygen Index
Glow Wire Flammability Index
0.75mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.75mm
High Amperage Arc Ignition Resistance
0.71mm
High Voltage Arc Tracking Rate
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-12
IEC 60695-2-13
UL 746A
UL 746A
UL 746A
|
%
℃
℃
arcs
mm/min(in/min)
s
|
HB
HB
24
650
650
800
675
>200
32.2(1.27)
12
7
8
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
125
120
125
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Other
Density
Water Absorption
Equilibrium 50%RH
Immersion 24h
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 1.6mm(0.063in)
Flow, 3.2mm(0.126in)
Flow, 6.4mm(0.25in)
Transverse, 1.6mm(0.063in)
Transverse, 3.2mm(0.126in)
Transverse, 6.4mm(0.25in)
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1230(1.23)
2.2
1.7
7.6
1.2
0.7
0.6
0.7
0.9
1.2
1.4
1.7
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|
PA66 加拿大杜邦 72G33HS1L-BK192
PA66 加拿大杜邦 77G33HS1L NC010
PA66 加拿大杜邦 77G33L-BK031
PA66 加拿大杜邦 HTHFE8200 NC010
PA66 加拿大杜邦 FR50-NC010
PA66 欧盟杜邦 101L NC010
PA66 欧盟杜邦 13T1 BKB145
PA66 欧盟杜邦 70GB40HSL
PA66 欧盟杜邦 FR72G25 V0
PA66 欧盟杜邦 FR72G25 V0 NC010
PA66 新加坡杜邦 101F
PA66 新加坡杜邦 101L
PA66 新加坡杜邦 101L NC010
PA66 新加坡杜邦 103FHS NC010
PA66 新加坡杜邦 103HSL NC010
PA66 加拿大杜邦 80G33L
PA66 加拿大杜邦 ST701HS
PA66 香港建德 6615G
PA66 香港建德 NB6615G
PA66 香港建德 NB6630G
PA66 香港毅兴行 E0488
PA66 香港毅兴行 E2136
PA66 新加坡美乐 R-NH6601
PA66 新加坡美乐 R-NH6602
PA66 新加坡美乐 RQ6630G
PA66 浙江华峰 EP-158
PA66 浙江华峰 EP-158N
诚信经营 质量保证 原厂原包 销售热线:18551213137 谭先生 网址:www.pa66-suliao.com