DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Toughened Resins
增韧树脂
Zytel® ST801AW BK195 is a Super Tough, weatherable, easy flow and processing friendly, black polyamide 66 resin for injection molding. It offers the best resistance to outdoor exposure.
zytel®ST801AW BK195是一个超级强韧,耐候性,易流动和加工友好,黑色尼龙66树脂注塑成型。它提供了最好的抗户外暴露。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-HI
>PA66-HI<
|
|
Mechanical
Yield Stress
Stress at Break
50mm/min
Tensile Stress
@ 50% Strain
Strain at Break
50mm/min
Nominal Strain at Break
Yield Strain
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
23℃(73℉)
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
%
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
47(6.8)
45(6.5)
50(7.2)
75
48
30
1900(276)
1800(261)
19
79
NB
|
41(5.9)
>50
1237(179)
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-30-30℃(-22-86℉)
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-30-30℃(-22-86℉)
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
162(324)
62(144)
262(504)
1.1(0.6)
1.0(0.6)
1.3(0.7)
1.3(0.7)
1.2(0.7)
1.1(0.6)
1.5(0.9)
1.5(0.9)
|
|
Electrical
Surface Resistivity
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
CTI
CTI
3.0mm
|
IEC 60093
IEC 60250
IEC 60093
IEC 60250
IEC 60243-1
IEC 60112
UL 746A
|
ohm
ohm m
E-4
kV/mm
V
V
|
2.4E16
3.9
3.7
2.0E14
60
120
25
600
600
|
3.0E12
6.7
4.0
7.4E10
1590
440
22
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Flammability
Flammability Classification
0.75mm
Flammability Classification
0.75mm
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
150
150
150
19
28
73
|
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
RTI, Strength
0.75mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
125
75
85
|
|
Other
Density
Water Absorption
Immersion 24h
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1090(1.09)
1.07
2.0
2.2
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
270-300(520-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2005.