DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G35NOX BK309 is a 35% glass reinforced, polyamide 66 resin developed for Selective Catalytic Reduction applications that require exposure to water/urea solution.
zytel®70G35NOX BK309是一个35%玻璃纤维增强聚酰胺66树脂,用于选择性催化还原的应用需要接触到水/尿素溶液。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Mechanical
Stress at Break
5mm/min
Strain at Break
5mm/min
Tensile Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
2
kJ/m
|
220(32)
3
12000(1740)
12
80
|
140(20.3)
5
8300(1200)
15
90
|
Thermal
Deflection Temperature
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
252(485)
263(505)
|
|
Other
Density
|
ISO 1183
|
|
1410(1.41)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Processing - Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(180)
<0.2
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The above data are preliminary and are subject to change as additional data are developed on subsequent lots.