PA66 RF203H 含玻璃纤维和专有润滑剂,医疗级
  • 产 品:PA66 RF203H 含玻璃纤维和专有润滑剂,医疗级
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP LUBRILOY* POLYAMIDES COMPOUND
TOUGH & STRONG -- WITH UNIQUE LUBRICITY
Polyamide-based LNP Lubriloy compounds provide enhanced lubrication through a unique, patented lubrication technology.

LNP™ LUBRILOY™ Compound PA66 RF203H 塑料物性表

Also known as:LNP™ Lubriloy™ Compound RF-15
Product reorder name:RF203H
LNP LUBRILOY* RF203H is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated, Healthcare

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 880 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 3.7 % ASTM D 638
Tensile Modulus,5mm/min 49800 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 1300 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 42600 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 90 MPa ISO 527
Tensile Strain,break,5mm/min 3.8 % ISO 527
Flexural Stress 140 MPa ISO 178
Flexural Modulus,2mm/min 5500 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 65 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 8 cm-kgf/cm ASTM D 256
Izod Impact,unnotched 80*10*4 +23℃ 30 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 9 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 232 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.12 - ASTM D 792
Density 1.13 g/cm³ ASTM D 792
Wear Factor Washer 70 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.36 - ASTM D 3702 Modified
Static COF 0.3 - ASTM D 3702 Modified
Density 1.13 g/cm³ ISO 1183
Source GMD,last updated:2012/08/29
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 270-280
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 80-95
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2012/08/29

 

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ LUBRILOY™ Compound PA66 RF203H