- 产 品：PBT K3501 热稳定,冲击改进,填充树脂
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.
Valox* Resin PBT K3501 数据表
Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive underhood applications requiring USCAR-2 Class III humidity/heat performance.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 500 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 240 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 3.5 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 51 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 24700 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 720 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 21200 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,50mm/min | 50 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 73 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 3.2 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 37 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2020 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 73 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2020 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,-30℃ | NB | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 9 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,0℃ | 8 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-20℃ | 7 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 489 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-40℃ | 611 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 -30℃ | NB | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 8 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 127 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 46 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 9.10E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 9.70E-05 | 1/℃ | ISO 11359-2 |
| Ball Pressure Test,75℃ +/- 2℃ | NA | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/50 | 170 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 170 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 46 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage,flow,3.2mm(5) | 1.7-2.6 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm(5) | 1.7-2.6 | % | SABIC Method |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.34 | % | ISO 62 |
| Moisture Absorption(23℃/50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate,MVR at 250℃/2.16 kg | 26 | cm³/10 min | ISO 1133 |
| AFTER 40 CYCLES,SIMILAR TO USCAR-2,CLASS III | Value | Unit | Standard |
| Tensile Stress,brk,Type I,50mm/min | 370 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 12 | % | ASTM D 638 |
| Flexural Modulus,1.3mm/min,50mm span | 24000 | kgf/cm² | ASTM D 790 |
| Instrumented Impact,Total Energy,23℃ | 590 | cm-kgf | ASTM D 3763 |
| PROPERTIES AFTER 1008 HOURS AT 125?C | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 550 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 4 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 25 | % | ASTM D 638 |
| Flexural Modulus,1.3mm/min,50mm span | 23700 | kgf/cm² | ASTM D 790 |
| Instrumented Impact,Total Energy,23℃ | 620 | cm-kgf | ASTM D 3763 |
| Source GMD,last updated:2004/04/02 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 60-75 | ℃ |
| Drying Time | 4-5 | hrs |
| Drying Time(Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 250-265 | ℃ |
| Nozzle Temperature | 245-260 | ℃ |
| Front-Zone 3 Temperature | 250-265 | ℃ |
| Middle-Zone 2 Temperature | 245-260 | ℃ |
| Rear-Zone 1 Temperature | 240-255 | ℃ |
| Mold Temperature | 65-90 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 50-80 | rpm |
| Shot to Cylinder Size | 40-80 | % |
| Vent Depth | 0.025-0.038 | mm |
| Source GMD,last updated:2004/04/02 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.POM F25-03 中粘度
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【Valox* Resin PBT K3501】