PBT V8280 含40玻璃纤维增强,外观良好
  • 产 品:PBT V8280 含40玻璃纤维增强,外观良好
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT V8280 数据表
40% GR PBT+PET. High stiffness. Excellent surface aesthetics. Applications include office furniture.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1480 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 1480 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 2.2 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.2 % ASTM D 638
Tensile Modulus,5mm/min 130000 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 2240 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 108900 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 84 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 10 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 80 cm-kgf ASTM D 3763
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 221 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 215 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 193 ASTM D 648
CTE,-40℃ to 40℃,flow 1.44E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.38E-05 1/℃ ASTM E 831
PHYSICAL Value Unit Standard
Specific Gravity 1.64 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.2-0.5 % SABIC Method
Mold Shrinkage,xflow,3.2mm(5) 0.5-0.8 % SABIC Method
Melt Flow Rate,266℃/5.0 kgf 33 g/10 min ASTM D 1238
Source GMD,last updated:2011/02/09
Parameter Injection Molding Value Unit
Drying Temperature 135
Drying Time 4-6 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 270-280
Nozzle Temperature 270-280
Front-Zone 3 Temperature 270-280
Middle-Zone 2 Temperature 270-280
Rear-Zone 1 Temperature 260-275
Mold Temperature 40-65
Back Pressure 0.3-0.7 MPa
Screw Speed 50-80 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
Source GMD,last updated:2011/02/09

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.m-PPE AN70 阻燃V-0级
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【Valox* Resin PBT V8280