PBT VX5022H 玻璃纤维20%增强,PBT+PC共混物,低翘曲
  • 产 品:PBT VX5022H 玻璃纤维20%增强,PBT+PC共混物,低翘曲
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT VX5022H 数据表
VALOX VX5022H is a 20% glass fiber reinforced PBT+PC blend with low warpage characteristics. This grade is VX5022 with a modified release package for part/mold designs that require enhanced de-molding characteristics.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yield,5mm/min 100 MPa ISO 527
Tensile Stress,break,5mm/min 100 MPa ISO 527
Tensile Strain,yield,5mm/min 2 % ISO 527
Tensile Strain,break,5mm/min 2 % ISO 527
Tensile Modulus,1mm/min 7000 MPa ISO 527
Flexural Stress,break,2mm/min 145 MPa ISO 178
Flexural Modulus,2mm/min 5000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched 80*10*4 +23℃ 40 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 40 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 7 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 6 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 6 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 5 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 40 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 35 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
CTE,23℃ to 60℃,flow 4.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 1.00E-04 1/℃ ISO 11359-2
CTE,23℃ to 80℃,flow 4.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 1.00E-04 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 140 ISO 306
Vicat Softening Temp,Rate B/120 144 ISO 306
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 120 ISO 75/Ae
PHYSICAL Value Unit Standard
Density 1.39 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.1 % ISO 62
Moisture Absorption(23℃/50% RH) 0.06 % ISO 62
Melt Volume Rate,MVR at 250℃/2.16 kg 13 cm³/10 min ISO 1133
Source GMD,last updated:2010/06/14
Parameter Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-270
Nozzle Temperature 240-260
Front-Zone 3 Temperature 245-265
Middle-Zone 2 Temperature 240-255
Rear-Zone 1 Temperature 230-245
Hopper Temperature 40-60
Mold Temperature 40-100
Source GMD,last updated:2010/06/14

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.TPV价格
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【Valox* Resin PBT VX5022H