- 产 品：PBT 1760 PBT+PC合金,玻纤11%增强,耐化学品腐蚀
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Xenoy* Resin
Xenoy* Resin All Series
Xenoy* alloys are a blend of semi-crystalline polyester (typically polybutylene terephthalate, PBT, or polyethylene terephthalate, PET) and polycarbonate (PC). The Xenoy family offers good chemical resistance, great impact resistance and toughness even at low temperatures, heat resistance, and outstanding aesthetic and flow characteristics.
XENOY™ Resin PBT+PC 1760 数据表
11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 850 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 850 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 3 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 4 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 54200 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 1330 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 39800 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 84 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 84 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 3 | % | ISO 527 |
| Tensile Strain,break,5mm/min | 2 | % | ISO 527 |
| Tensile Modulus,1mm/min | 4950 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 134 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 4050 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 9 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 8 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact,Energy @ peak,-20℃ | 40 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Energy @ peak,-30 | 30 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,23℃ | 81 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-30℃ | 30 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 3 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 3 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 16 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 121 | ℃ | ASTM D 1525 |
| HDT,1.82 MPa,6.4mm,unannealed | 115 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 7.70E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 3.80E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 95℃,flow | 4.50E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 95℃,xflow | 7.38E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 7.70E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 3.80E-05 | 1/℃ | ISO 11359-2 |
| Vicat Softening Temp,Rate B/50 | 135 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 130 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 104 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.3 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm(5) | 0.4-0.6 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm(5) | 0.4-0.6 | % | SABIC Method |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.5 | % | ISO 62 |
| Moisture Absorption(23℃/50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate,MVR at 265℃/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| Source GMD,last updated:2011/02/04 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 110 | ℃ |
| Drying Time | 4-6 | hrs |
| Drying Time(Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260-280 | ℃ |
| Nozzle Temperature | 255-275 | ℃ |
| Front-Zone 3 Temperature | 260-280 | ℃ |
| Middle-Zone 2 Temperature | 255-275 | ℃ |
| Rear-Zone 1 Temperature | 250-270 | ℃ |
| Mold Temperature | 65-95 | ℃ |
| Back Pressure | 0.3-0.6 | MPa |
| Screw Speed | 50-80 | rpm |
| Shot to Cylinder Size | 50-80 | % |
| Vent Depth | 0.013-0.02 | mm |
| Source GMD,last updated:2011/02/04 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.m-PPE AV90 阻燃V-1级
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【XENOY™ Resin PBT+PC 1760】