PBT HX5600HP 耐化学,医疗级,抗冲击
  • 产 品:PBT HX5600HP 耐化学,医疗级,抗冲击
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Xenoy* Resin
Xenoy* Resin All Series
Xenoy* alloys are a blend of semi-crystalline polyester (typically polybutylene terephthalate, PBT, or polyethylene terephthalate, PET) and polycarbonate (PC). The Xenoy family offers good chemical resistance, great impact resistance and toughness even at low temperatures, heat resistance, and outstanding aesthetic and flow characteristics.

XENOY™ Resin PBT HX5600HP 数据表
Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 500 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 530 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 5 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 150 % ASTM D 638
Tensile Modulus,5mm/min 21400 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 710 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 20300 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 50 MPa ISO 527
Tensile Stress,break,50mm/min 55 MPa ISO 527
Tensile Strain,yield,50mm/min 5 % ISO 527
Tensile Strain,break,50mm/min 100 % ISO 527
Tensile Modulus,1mm/min 2050 MPa ISO 527
Flexural Stress,yield,2mm/min 75 MPa ISO 178
Flexural Modulus,2mm/min 2050 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 76 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 61 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 815 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 -40℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 55 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 25 kJ/m² ISO 180/1A
Charpy -30℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 60 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 125 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 80 ASTM D 648
CTE,-40℃ to 40℃,flow 9.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 9.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 9.00E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 9.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,flow 1.00E-04 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 125 ISO 306
Vicat Softening Temp,Rate B/120 123 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 105 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 80 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.22 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.7-1.1 % SABIC Method
Melt Flow Rate,250℃/5.0 kgf 11 g/10 min ASTM D 1238
Density 1.22 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.4 % ISO 62
Moisture Absorption(23℃/50% RH) 0.05 % ISO 62
Melt Volume Rate,MVR at 250℃/5.0 kg 10 cm³/10 min ISO 1133
Melt Viscosity,260℃,1500 sec-1 260 Pa-s ISO 11443
Source GMD,last updated:2008/03/14
Parameter Injection Molding Value Unit
Drying Temperature 90-100
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 255-270
Nozzle Temperature 250-265
Front-Zone 3 Temperature 250-270
Middle-Zone 2 Temperature 240-265
Rear-Zone 1 Temperature 230-250
Hopper Temperature 40-60
Mold Temperature 60-80
Source GMD, last updated:2008/03/14

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.塑胶原料价格
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.