- 产 品：PC 4401R 高耐热的聚(酯)碳酸酯
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Lexan* Standard High Heat Resin
Moderate Heat Resistance
Our standard heat resistance grades offer a range of products suitable for moderate heat applications. These materials are based upon a unique polycarbonate copolymer technology that offers improved heat resistance and excellent impact performance. The Lexan XHT product portfolio offers even higher heat resistance and better processability for more demanding applications.
Lexan* Resin 4401R 英文数据物性表
LEXAN 4401R is a high heat resistant poly(ester)carbonate injection molding resin.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 670 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 710 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 7 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | >50 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 21400 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 960 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 22400 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,50mm/min | 65 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 60 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 6 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 85 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2150 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 100 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | NB | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 61 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 1223 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*3 +23℃ | NB | kJ/m² | ISO 180/1U |
| Izod Impact,unnotched 80*10*3 -30℃ | NB | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*3 +23℃ | 53 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*3 -30℃ | 11 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm | 54 | kJ/m² | ISO 179/1eA |
| Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm | 13 | kJ/m² | ISO 179/1eA |
| Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30℃,Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 166 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 148 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 142 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 8.00E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 8.00E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 8.00E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 8.00E-05 | 1/℃ | ISO 11359-2 |
| Ball Pressure Test,125℃ +/- 2℃ | pass | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/50 | 155 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 157 | ℃ | ISO 306 |
| HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm | 149 | ℃ | ISO 75/Be |
| HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm | 137 | ℃ | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar,flow (2) (5) | 0.6-0.8 | % | SABIC Method |
| Mold Shrinkage,flow,3.2mm (5) | 0.6-0.8 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm (5) | 0-0.2 | % | SABIC Method |
| Melt Flow Rate,300℃/1.2 kgf | 6 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.16 | % | ISO 62 |
| Moisture Absorption (23℃ / 50% RH) | 0.35 | % | ISO 62 |
| Melt Volume Rate,MVR at 300℃/1.2 kg | 6 | cm³/10 min | ISO 1133 |
| Melt Volume Rate,MVR at 330℃/2.16kg | 29 | cm³/10 min | ISO 1133 |
| Source GMD,last updated:2003/11/06 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120 | ℃ |
| Drying Time | 2-4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 290-320 | ℃ |
| Nozzle Temperature | 280-310 | ℃ |
| Front-Zone 3 Temperature | 290-320 | ℃ |
| Middle-Zone 2 Temperature | 280-310 | ℃ |
| Rear-Zone 1 Temperature | 270-300 | ℃ |
| Hopper Temperature | 60-80 | ℃ |
| Mold Temperature | 80-120 | ℃ |
| Source GMD,last updated:2003/11/06 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.