- 产 品：PC FXG154 PC钻石效果颜色
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Lexan* Visualfx* Resin
Beauty Is More Than Skin Deep
Lexan Polycarbonate Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Diamond, Luminescent, Diffusion, Lustre, and Edge Glow, as well as several metallic and natural material effects. Available in a variety of colors and base resins.
Lexan* Resin FXG154 英文物性表
FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.
Property
TYPICAL PROPERTIES(1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 590 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 580 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 5.9 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 39 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 27300 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 990 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 24300 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 61 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 54 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 6.2 | % | ISO 527 |
| Tensile Strain,break,5mm/min | 75 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2430 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 94 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2340 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 76 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 14 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 632 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 51 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 16 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 58 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 153 | ℃ | ASTM D 1525 |
| HDT,1.82 MPa,3.2mm,unannealed | 133 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 7.00E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 7.00E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 7.00E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 7.00E-05 | 1/℃ | ISO 11359-2 |
| Vicat Softening Temp,Rate B/50 | 147 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 149 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 129 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm (5) | 0.5-0.7 | % | SABIC Method |
| Melt Flow Rate,200℃/3.8 kgf | 2.5 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.15 | % | ISO 62 |
| Moisture Absorption (23℃/50%RH) | 0.09 | % | ISO 62 |
| Melt Volume Rate,MVR at 220℃/5.0 kg | 2 | cm³/10 min | ISO 1133 |
| Source GMD,last updated:2007/03/14 | |||
| Parameter Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 120 | ℃ |
| Drying Time | 2-4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Minimum Moisture Content | 0.01 | % |
| Melt Temperature (Parison) | 265-280 | ℃ |
| Barrel-Zone 1 Temperature | 260-290 | ℃ |
| Barrel-Zone 2 Temperature | 260-290 | ℃ |
| Barrel-Zone 3 Temperature | 260-290 | ℃ |
| Barrel-Zone 4 Temperature | 260-290 | ℃ |
| Adapter-Zone 5 Temperature | 260-290 | ℃ |
| Mold Temperature | 60-100 | ℃ |
| Source GMD,last updated:2007/03/14 | ||
• Uncontaminated regrind up to 25% is allowed.
• Screw configuration affects melt temperature. A low shear, 2.5:1
• Mold temperatures of 65℃-95℃(150℉-200℉) produce best surface appearance.
• 15-50 rpm screw speed suggested. Adjust actural rpm for desired output while maintaining desired melt temperature range. Increasing screw speed increases shear heating; use a hand-held pyrometer to measure melt temperature. Adjust barrel temperatures to maintain recommended melt temperature range.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.