Lexan* Resin PC0700 英文物性表
PC0700 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It is available exclusivPC0700 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It is available exclusively at www.pa66-suliao.com.

Property
TYPICAL PROPERTIES(1)

MECHANICAL Value Unit  Standard 
Tensile Stress,yld,Type I,50mm/min 640 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 6 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min >70 % ASTM D 638
Tensile Modulus,50mm/min 23900 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 910 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 23400 kgf/cm² ASTM D 790
Hardness,Rockwell R 120 - ASTM D 785
Tensile Stress,yield,50mm/min 63 MPa ISO 527
Tensile Strain,yield,50mm/min 6 % ISO 527
Tensile Strain,break,50mm/min >70 % ISO 527
Tensile Modulus,1mm/min 2350 MPa ISO 527
Flexural Stress,yield,2mm/min 90 MPa ISO 178
Flexural Modulus,2mm/min 2300 MPa ISO 178
Hardness,Rockwell R 120 - ISO 2039-2
IMPACT Value Unit  Standard 
Izod Impact,unnotched,23℃ NB cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 91 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 662 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*3 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*3 -30℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*3 +23℃ 70 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 12 kJ/m² ISO 180/1A
THERMAL Value Unit  Standard 
Vicat Softening Temp,Rate B/50 144 ASTM D 1525
HDT,0.45 MPa,3.2mm 138 ASTM D 648
HDT,1.82 MPa,3.2mm 127 ASTM D 648
CTE,-40℃ to 95℃,flow 7.00E-05 1/℃ ASTM E 831
Thermal Conductivity 0.2 W/m-℃ ASTM C 177
Thermal Conductivity 0.2 W/m-℃ ISO 8302
CTE,23℃ to 80℃,flow 7.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ Passes - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 144 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 138 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 127 ISO 75/Af
PHYSICAL Value Unit  Standard 
Specific Gravity 1.2 - ASTM D 792
Water Absorption,equilibrium,23C 0.35 % ASTM D 570
Mold Shrinkage on Tensile Bar,flow (2) (5) 0.5-0.7 % SABIC Method
Mold Shrinkage,flow,3.2mm (5) 0.5-0.7 % SABIC Method
Melt Flow Rate,300℃/1.2 kgf 7 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.35 % ISO 62
Melt Volume Rate,MVR at 300℃/1.2 kg 6 cm³/10 min ISO 1133
OPTICAL Value Unit  Standard 
Light Transmission,2.54mm 88-90 % ASTM D 1003
Haze,2.54mm <0.8 % ASTM D 1003
Refractive Index 1.586 - ASTM D 542
Refractive Index 1.586 - ISO 489
ELECTRICAL Value Unit  Standard 
Volume Resistivity >1.E+15 Ohm-cm ASTM D 257
Dielectric Strength,1.6mm 27 kV/mm ASTM D 149
Relative Permittivity,60 Hz 3 - ASTM D 150
Relative Permittivity,1 MHz 3 - ASTM D 150
Dissipation Factor,60 Hz 0.001 - ASTM D 150
Dissipation Factor,1 MHz 0.01 - ASTM D 150
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Dielectric Strength,1.6mm 27 kV/mm IEC 60243-1
Relative Permittivity,60 Hz 3 - IEC 60250
Relative Permittivity,1 MHz 3 - IEC 60250
Dissipation Factor,60 Hz 0.001 - IEC 60250
Dissipation Factor,1 MHz 0.01 - IEC 60250
FLAME CHARACTERISTICS Value Unit  Standard 
UL Recognized,94V-2 Flame Class Rating (3) 1.6 mm UL 94
Source GMD,last updated:2012/03/16

Parameter Injection Molding Value Unit 
Drying Temperature 120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 290-320
Nozzle Temperature 280-310
Front-Zone 3 Temperature 290-320
Middle-Zone 2 Temperature 280-310
Rear-Zone 1 Temperature 270-300
Hopper Temperature 60-80
Mold Temperature 80-120
Source GMD,last updated:2012/03/16
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.