PC D1000P 聚碳酸酯树脂化合物,易处理
  • 产 品:PC D1000P 聚碳酸酯树脂化合物,易处理
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* Colorcomp* Compound
LNP Colorcomp All Series
LNP* Colorcomp* resins contain colorants and special effects for a dazzling spectrum of colored materials. Among the offerings are opaque, translucent, and transparent resins, plus special effects, including edge glow, sparkle, glow, pearlescent, and thermochromic. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™Colorcomp™ Compound PC D1000P 数据
Also known as:LNP™Colorcomp™Compound D-1000 EP RD1-934 TP
Product reorder name:D1000P
LNP* Colorcomp* D1000P is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Exceptional Processing.

MECHANICAL Value Unit Standard
Tensile Stress,yield 630 kgf/cm² ASTM D 638
Tensile Stress,break 570 kgf/cm² ASTM D 638
Tensile Strain,yield 5.3 % ASTM D 638
Tensile Strain,break 78.7 % ASTM D 638
Tensile Modulus,50mm/min 21000 kgf/cm² ASTM D 638
Flexural Modulus 28100 kgf/cm² ASTM D 790
Tensile Stress,yield 64 MPa ISO 527
Tensile Stress,break 59 MPa ISO 527
Tensile Strain,yield 5.6 % ISO 527
Tensile Strain,break 87 % ISO 527
Tensile Modulus,1mm/min 2210 MPa ISO 527
Flexural Stress 81 MPa ISO 178
Flexural Modulus 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 55 cm-kgf/cm ASTM D 256
Izod Impact,notched 80*10*4 +23℃ 13 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 123 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 124 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.2 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.6-0.8 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.7-0.9 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.65 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.75 % ISO 294
Density 1.19 g/cm³ ISO 1183
Source GMD,last updated:2008/09/24
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 300-315
Front-Zone 3 Temperature 310-320
Middle-Zone 2 Temperature 305-315
Rear-Zone 1 Temperature 295-305
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2008/09/24

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.PC/ABS MC8100 挤出吹塑级
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™Colorcomp™ Compound PC D1000P