PC DS0036IP 导电级,EMI/RFI屏蔽,耐冲击,无溴氯阻燃
  • 产 品:PC DS0036IP 导电级,EMI/RFI屏蔽,耐冲击,无溴氯阻燃
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP Faradex* Polycarbonate Compound
Tough electromagnetic and RFI control
Polycarbonate-based LNP Faradex compounds provide electromagnetic and radio frequency interference (EMI/RFI) attenuation to this tough, stable resin family.

LNP™Faradex™ Compound PC DS0036IP 数据
Also known as:LNP™Faradex™Compound DS-1003 FR HI
Product reorder name:DS0036IP
LNP* Faradex* DS0036IP is a compound based on Polycarbonate resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, High Impact, Non-Brominated & Non-Chlorinated Flame Retardant.

MECHANICAL Value Unit Standard
Tensile Stress,yield 57 MPa ISO 527
Tensile Stress,break 55 MPa ISO 527
Tensile Strain,yield 3.8 % ISO 527
Tensile Strain,break 4-8 % ISO 527
Tensile Modulus,1mm/min 2800 MPa ISO 527
Flexural Stress 80 MPa ISO 178
Flexural Modulus 2600 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 182 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 12 cm-kgf/cm ASTM D 256
Izod Impact,unnotched 80*10*4 +23℃ 85 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 11 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
CTE,-40℃ to 40℃,flow 6.70E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 5.60E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 136 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 125 ISO 75/Af
PHYSICAL Value Unit Standard
Mold Shrinkage,flow,24 hrs(5) 0.4-0.7 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.5 % ISO 294
Density 1.29 g/cm³ ISO 1183
ELECTRICAL Value Unit Standard
Volume Resistivity 1.00E+04 Ohm-cm ASTM D 257
Surface Resistivity 1.E+02-1.E+03 Ohm ASTM D 257
Shielding Effectivness @ 3mm 40-55 dB SABIC Method
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 2.1 mm UL 94 by SABIC-IP
Source GMD,last updated:2007/04/23
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305-325
Front-Zone 3 Temperature 320-330
Middle-Zone 2 Temperature 310-320
Rear-Zone 1 Temperature 295-305
Mold Temperature 95-120
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2007/04/23

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.塑料是非线形材料
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™Faradex™ Compound PC DS0036IP