PC DAL22 含有聚四氟乙烯,芳纶纤维,内部润滑
  • 产 品:PC DAL22 含有聚四氟乙烯,芳纶纤维,内部润滑
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP Lubricomp* Polycarbonate Compound
Strong, tough -- and wear-resistant
Polycarbonate-based LNP Lubricomp compounds add wear resistance and lower the friction of polycarbonate by combining it with internal lubricants. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound PC DAL22 塑料数据

Also known as:LNP™ Lubricomp™ Compound DAL-4022
Product reorder name:DAL22
LNP* Lubricomp* DAL22 is a compound based on Polycarbonate resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,yield 610 kgf/cm² ASTM D 638
Tensile Stress,break 540 kgf/cm² ASTM D 638
Tensile Strain,yield 5.3 % ASTM D 638
Tensile Strain,break 8.8 % ASTM D 638
Tensile Modulus,50mm/min 28100 kgf/cm² ASTM D 638
Flexural Stress 1330 kgf/cm² ASTM D 790
Flexural Modulus 28100 kgf/cm² ASTM D 790
Tensile Stress,yield 59 MPa ISO 527
Tensile Stress,break 57 MPa ISO 527
Tensile Strain,yield 5.2 % ISO 527
Tensile Strain,break 8 % ISO 527
Tensile Modulus,1mm/min 2820 MPa ISO 527
Flexural Stress 84 MPa ISO 178
Flexural Modulus 3000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 73 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 5 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 111 cm-kgf ASTM D 3763
Multiaxial Impact 36 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 41 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 137 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 127 ASTM D 648
CTE,-40℃ to 40℃,flow 7.02E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 5.58E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 6.90E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 5.50E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 138 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 129 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.27 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.1 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.6 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.7 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.6 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.71 % ISO 294
Wear Factor Washer 21 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.28 - ASTM D 3702 Modified
Static COF 0.18 - ASTM D 3702 Modified
Density 1.27 g/cm³ ISO 1183
Source GMD,last updated:2007/08/02
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 300-315
Front-Zone 3 Temperature 310-320
Middle-Zone 2 Temperature 305-315
Rear-Zone 1 Temperature 295-305
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD, last updated:2007/08/02

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.