PC D2000P 含专有的润滑剂聚碳酸酯树脂
  • 产 品:PC D2000P 含专有的润滑剂聚碳酸酯树脂
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* LUBRILOY* COMPOUND
LNP LUBRILOY RESIN ALL SERIES
LNP* Lubriloy* alloy composites provide lubrication through a unique, patented lubrication technology. Lubriloy* composites feature high impact and toughness and are used in a variety of demanding automotive, office equipment, electronics, and appliance applications. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ LUBRILOY™ Compound PC D2000P 塑料数据

Also known as:LNP™ Lubriloy™ Compound D-EP
Product reorder name:D2000P
LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing.

MECHANICAL Value Unit Standard
Tensile Stress,yield 570 kgf/cm² ASTM D 638
Tensile Stress,break 470 kgf/cm² ASTM D 638
Tensile Strain,yield 5.9 % ASTM D 638
Tensile Strain,break 42.3 % ASTM D 638
Tensile Modulus,50mm/min 19600 kgf/cm² ASTM D 638
Flexural Stress 880 kgf/cm² ASTM D 790
Flexural Modulus 23200 kgf/cm² ASTM D 790
Tensile Stress,yield 54 MPa ISO 527
Tensile Stress,break 46 MPa ISO 527
Tensile Strain,yield 5.3 % ISO 527
Tensile Strain,break 43.1 % ISO 527
Tensile Modulus,1mm/min 2100 MPa ISO 527
Flexural Stress 86 MPa ISO 178
Flexural Modulus 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ NB cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 46 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 410 cm-kgf ASTM D 3763
Multiaxial Impact 441 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 137 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 12 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 137 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 125 ASTM D 648
CTE,-40℃ to 40℃,flow 7.12E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.27E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 7.12E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.28E-05 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 131 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.17 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.13 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.8 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.8 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.84 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.81 % ISO 294
Wear Factor Washer 44 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.19 - ASTM D 3702 Modified
Static COF 0.15 - ASTM D 3702 Modified
Density 1.17 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.21 % ISO 62
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94HB Flame Class Rating(3)(4) 1.5 mm UL 94 by SABIC-IP
Source GMD,last updated:2004/09/30
Parameter Injection Molding Value Unit
Drying Temperature 100
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305-315
Front-Zone 3 Temperature 305-315
Middle-Zone 2 Temperature 300-310
Rear-Zone 1 Temperature 295-305
Mold Temperature 65-95
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.