LNP STAT-KON* POLYCARBONATE COMPOUND
STRENGTH PLUS TAILORED ELECTRICAL PROPERTIES
Polycarbonate-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound PC DE002ER 塑料物性表

Also known as:LNP™ Stat-kon™ Compound DC-1002 EM MR
Product reorder name:DE002ER
LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.

MECHANICAL Value Unit Standard
Tensile Stress,break 1020 kgf/cm² ASTM D 638
Tensile Strain,break 2.8 % ASTM D 638
Tensile Modulus,50mm/min 71000 kgf/cm² ASTM D 638
Flexural Stress 1680 kgf/cm² ASTM D 790
Flexural Modulus 62500 kgf/cm² ASTM D 790
Tensile Stress,break 102 MPa ISO 527
Tensile Strain,break 3.3 % ISO 527
Tensile Modulus,1mm/min 6800 MPa ISO 527
Flexural Stress 170 MPa ISO 178
Flexural Modulus 6960 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 57 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 202 cm-kgf ASTM D 3763
Multiaxial Impact 43 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 39 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 7 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 143 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 141 ASTM D 648
CTE,-40℃ to 40℃,flow 2.64E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 5.83E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 2.65E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 5.83E-05 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 142 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.23 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.17 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.1-0.3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.2-0.4 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.06-0.32 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.29-0.43 % ISO 294
Density 1.23 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.66 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+02-1.E+06 Ohm ASTM D 257
Source GMD,last updated:2004/09/30
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305-325
Front-Zone 3 Temperature 320-330
Middle-Zone 2 Temperature 310-320
Rear-Zone 1 Temperature 295-305
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD, last updated:2004/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.