PC DE003Z 含有碳纤维,导电聚碳酸酯
  • 产 品:PC DE003Z 含有碳纤维,导电聚碳酸酯
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP STAT-KON* POLYCARBONATE COMPOUND
STRENGTH PLUS TAILORED ELECTRICAL PROPERTIES
Polycarbonate-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound PC DE003Z 塑料物性表

Also known as:LNP™ Stat-kon™ Compound DC-1003 E
Product reorder name:DE003Z
LNP STAT-KON* DE003Z is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1360 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 1360 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.4 % ASTM D 638
Tensile Modulus,5mm/min 115400 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 2030 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 92900 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 130 MPa ISO 527
Tensile Strain,break,5mm/min 2.6 % ISO 527
Tensile Modulus,1mm/min 10660 MPa ISO 527
Flexural Stress 191 MPa ISO 178
Flexural Modulus,2mm/min 9290 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 63 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 10 cm-kgf/cm ASTM D 256
Multiaxial Impact 45 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 251 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 39 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 147 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 144 ASTM D 648
CTE,-30℃ to 30℃,flow 2.20E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 4.80E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 147 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 143 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.26 - ASTM D 792
Density 1.253 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.13 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.1-0.3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.4-0.6 % ASTM D 955
Moisture Absorption(23℃/50% RH) 0.21 % ISO 62
Source GMD,last updated:2011/06/20
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305-325
Front-Zone 3 Temperature 320-330
Middle-Zone 2 Temperature 310-320
Rear-Zone 1 Temperature 295-305
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2011/06/20

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ STAT-KON™ Compound PC DE003Z