PC DEF42 含有碳纤维和玻璃纤维,导电聚碳酸酯
  • 产 品:PC DEF42 含有碳纤维和玻璃纤维,导电聚碳酸酯
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP STAT-KON* POLYCARBONATE COMPOUND
STRENGTH PLUS TAILORED ELECTRICAL PROPERTIES
Polycarbonate-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound PC DEF42 塑料物性表

Also known as:LNP™ Stat-kon™ Compound DCF-1006
Product reorder name:DEF42
LNP STAT-KON* DEF42 is a compound based on Polycarbonate resin containing Carbon Fiber, Glass Fiber. Added features of this material include: Electrically Conductive.

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 1250 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 2.3 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.4 % ASTM D 638
Tensile Modulus,50mm/min 117200 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 1920 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 104000 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 125 MPa ISO 527
Tensile Strain,yield,5mm/min 2.4 % ISO 527
Tensile Strain,break,5mm/min 2.6 % ISO 527
Tensile Modulus,1mm/min 11410 MPa ISO 527
Flexural Stress 186 MPa ISO 178
Flexural Modulus,2mm/min 10240 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 69 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 8 cm-kgf/cm ASTM D 256
Multiaxial Impact 41 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 150 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 41 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 145 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 142 ASTM D 648
CTE,-40℃ to 40℃,flow 1.60E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 5.50E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 1.60E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 5.50E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 146 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 143 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.41 - ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.88 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.06-0.08 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.4-0.6 % ASTM D 955
Density 1.4 g/cm³ ISO 1183
ELECTRICAL Value Unit Standard
Surface Resistivity 2.E+00-5.E+00 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-0 Flame Class Rating(3) 2.4 mm UL 94
Source GMD,last updated:2009/08/27
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305-325
Front-Zone 3 Temperature 320-330
Middle-Zone 2 Temperature 310-320
Rear-Zone 1 Temperature 295-305
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2009/08/27

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ STAT-KON™ Compound PC DEF42