Cycoloy* Auto Non-FR Resin
Non-Flame Retardant Resins for Automotive
A wide range of PC/ABS resin grades offer features such as low gloss, high heat, high impact resistance and others suitable for various automotive interior applications.
Cycoloy* Resin MC8100 数据
Extrusion blowmolding grade.
Property
TYPICAL PROPERTIES (1)
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50mm/min | 530 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,50mm/min | 5 | % | ASTM D 638 |
Tensile Strain,brk,Type I,50mm/min | 100 | % | ASTM D 638 |
Tensile Modulus,50mm/min | 21000 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3mm/min,50mm span | 780 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3mm/min,50mm span | 21000 | kgf/cm² | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 54 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,-30℃ | 43 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Total Energy,23℃ | 553 | cm-kgf | ASTM D 3763 |
Instrumented Impact Total Energy,-30℃ | 483 | cm-kgf | ASTM D 3763 |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,3.2mm,unannealed | 123 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 104 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 8.10E-05 | 1/℃ | ASTM E 831 |
Thermal Conductivity | 0.2 | W/m-℃ | ASTM C 177 |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.13 | - | ASTM D 792 |
Water Absorption,24 hours | 0.1 | % | ASTM D 570 |
Water Absorption,equilibrium,23C | 0.4 | % | ASTM D 570 |
Mold Shrinkage,flow,3.2mm(5) | 0.4-0.7 | % | SABIC Method |
Source GMD,last updated:2000/01/05 |
Parameter Extrusion Blow Molding | Value | Unit |
Drying Temperature | 100-110 | ℃ |
Drying Time | 3-4 | hrs |
Drying Time(Cumulative) | 24 | hrs |
Maximum Moisture Content | 0.04-0.05 | % |
Minimum Moisture Content | 0.04 | % |
Melt Temperature(Parison) | 245-260 | ℃ |
Barrel-Zone 1 Temperature | 240-250 | ℃ |
Barrel-Zone 2 Temperature | 240-255 | ℃ |
Barrel-Zone 3 Temperature | 240-255 | ℃ |
Barrel-Zone 4 Temperature | 240-255 | ℃ |
Adapter-Zone 5 Temperature | 245-260 | ℃ |
Head-Zone 6-Top Temperature | 245-260 | ℃ |
Head-Zone 7-Bottom Temperature | 245-260 | ℃ |
Screw Speed | 20-50 | rpm |
Extruder Feed Zone Temperature | 60-80 | ℃ |
Mold Temperature | 40-90 | ℃ |
Die Temperature | 250-265 | ℃ |
Source GMD,last updated:2000/01/05 |
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.