PC/ABS C1200HFM 高耐热,良好的流动特性
  • 产 品:PC/ABS C1200HFM 高耐热,良好的流动特性
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin C1200HFM 数据
PC+ABS-MAGIX version in various metallic colors. High heat/good flow characteristics. Appliances, automotive/telecommunication.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit  Standard 
Tensile Stress,yld,Type I,50mm/min 520 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 450 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 5 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 50 % ASTM D 638
Tensile Modulus,50mm/min 25300 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 770 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 24600 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 55 MPa ISO 527
Tensile Stress,break,50mm/min 45 MPa ISO 527
Tensile Strain,yield,50mm/min 5 % ISO 527
Tensile Strain,break,50mm/min 15 % ISO 527
Tensile Modulus,1mm/min 2400 MPa ISO 527
Flexural Stress,yield,2mm/min 82 MPa ISO 178
Flexural Modulus,2mm/min 2400 MPa ISO 178
Hardness,H358/30 121 MPa ISO 2039-1
IMPACT Value Unit  Standard 
Izod Impact,notched,23℃ 43 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 414 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*4 +23℃ 24 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 12 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 25 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 13 kJ/m² ISO 179/1eA
THERMAL Value Unit  Standard 
Vicat Softening Temp,Rate B/50 143 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 131 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 112 ASTM D 648
CTE,-40℃ to 40℃,flow 7.20E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.20E-05 1/℃ ASTM E 831
Thermal Conductivity 0.2 W/m-℃ ISO 8302
CTE,23℃ to 80℃,flow 8.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 8.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 128 ISO 306
Vicat Softening Temp,Rate B/120 130 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 128 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 108 ISO 75/Ae
Relative Temp Index,Elec 105 UL 746B
Relative Temp Index,Mech w/impact 80 UL 746B
Relative Temp Index,Mech w/o impact 105 UL 746B
PHYSICAL Value Unit  Standard 
Specific Gravity 1.18 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.4-0.6 % SABIC Method
Melt Flow Rate,260℃/5.0 kgf 22 g/10 min ASTM D 1238
Density 1.18 g/cm³ ISO 1183
Melt Volume Rate,MVR at 260℃/5.0 kg 22 cm³/10 min ISO 1133
ELECTRICAL Value Unit  Standard 
Arc Resistance,Tungsten{PLC} 3 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 3 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 0 PLC Code UL 746A
Source GMD,last updated:2001/04/11
Parameter Injection Molding Value Unit 
Drying Temperature 105-110
Drying Time 3-4 hrs
Drying Time(Cumulative) 8 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 275-300
Nozzle Temperature 275-300
Front-Zone 3 Temperature 260-300
Middle-Zone 2 Temperature 255-295
Rear-Zone 1 Temperature 250-290
Mold Temperature 60-90
Back Pressure 0.3-0.7 MPa
Screw Speed 40-70 rpm
Shot to Cylinder Size 30-80 %
Vent Depth 0.038-0.076 mm
Source GMD,last updated:2001/04/11
• NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.