PC/ABS CS9610 无溴无氯阻燃,最佳机械冲击平衡
  • 产 品:PC/ABS CS9610 无溴无氯阻燃,最佳机械冲击平衡
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for.
This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects.
Available in a variety of colors and base resins.

Cycoloy* Resin CS9610 数据
Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior. This grade potentially can be considered for a wide variety of applications in areas such as transportation, consumer electronics and electrical equipments.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 650 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 630 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 5 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 55 % ASTM D 638
Tensile Modulus,50mm/min 26500 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 990 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 24800 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 62 MPa ISO 527
Tensile Stress,break,50mm/min 50 MPa ISO 527
Tensile Strain,yield,50mm/min 4.8 % ISO 527
Tensile Strain,break,50mm/min >45 % ISO 527
Tensile Modulus,1mm/min 2400 MPa ISO 527
Flexural Stress,yield,2mm/min 98 MPa ISO 178
Flexural Modulus,2mm/min 2500 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 81 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 734 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*3 +23℃ 45 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 15 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 45 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 15 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 118 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 105 ASTM D 648
Vicat Softening Temp,Rate B/50 124 ISO 306
Vicat Softening Temp,Rate B/120 127 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 106 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.4-0.6 % SABIC Method
Melt Flow Rate,260℃/5.0 kgf 15 g/10 min ASTM D 1238
Melt Volume Rate,MVR at 260℃/5.0 kg 12 cm³/10 min ISO 1133
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-0 Flame Class Rating(3) 2 mm UL 94
UL Recognized,94-5VB Rating(3) 2 mm UL 94
NBS Smoke Density,Flaming,Dmax 225 - ASTM E 662
NBS Smoke Density,Flaming,Ds 1.5 min 40 - ASTM E 662
NBS Smoke Density,Flaming,Ds 4 min 150 - ASTM E 662
Source GMD,last updated:2007/10/15
Parameter Injection Molding Value Unit
Drying Temperature 90
Drying Time 4 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 270-300
Nozzle Temperature 265-300
Front-Zone 3 Temperature 265-300
Middle-Zone 2 Temperature 260-300
Rear-Zone 1 Temperature 260-300
Hopper Temperature 60-80
Mold Temperature 60-90
Back Pressure 0.3-0.7 MPa
Screw Speed 40-70 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.038-0.076 mm
Source GMD,last updated:2007/10/1
• NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.