PC/ABS CY5005 非溴氯阻燃,水解稳定,流动优异
  • 产 品:PC/ABS CY5005 非溴氯阻燃,水解稳定,流动优异
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin CY5005 数据
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applications including business equipment, TV enclosures, among others

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50 mm/min 660 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50 mm/min 480 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50 mm/min 3.9 % ASTM D 638
Tensile Strain,brk,Type I,50 mm/min 34 % ASTM D 638
Tensile Modulus,5 mm/min 28500 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 980 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 26800 kgf/cm² ASTM D 790
Tensile Stress,yield,50 mm/min 63 MPa ISO 527
Tensile Stress,break,50 mm/min 43 MPa ISO 527
Tensile Strain,yield,50 mm/min 3.5 % ISO 527
Tensile Strain,break,50 mm/min 40 % ISO 527
Tensile Modulus,1 mm/min 2670 MPa ISO 527
Flexural Stress,yield,2 mm/min 95 MPa ISO 178
Flexural Modulus,2 mm/min 2700 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 7 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 203 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*3 +23℃ 10 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 5 kJ/m² ISO 180/1A
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 5 kJ/m² ISO 179/1eA
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 10 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
HDT,1.82 MPa,6.4 mm,unannealed 81 ASTM D 648
CTE,-40℃ to 40℃,flow 7.50E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.50E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 89 ISO 306
Vicat Softening Temp,Rate B/120 92 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 73 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.18 - ASTM D 792
Mold Shrinkage,flow,3.2 mm(5) 0.4-0.6 % SABIC Method
Melt Flow Rate,260℃/2.16 kgf 31 g/10 min ASTM D 1238
Density 1.18 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.1 % ISO 62
Moisture Absorption(23℃/50% RH) 0.05 % ISO 62
Melt Volume Rate,MVR at 260℃/2.16 kg 27 cm³/10 min ISO 1133
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 2 mm UL 94 by SABIC-IP
Source GMD,last updated:2012/07/30
Parameter Injection Molding Value Unit
Drying Temperature 75-80
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 230-270
Nozzle Temperature 220-260
Front-Zone 3 Temperature 230-270
Middle-Zone 2 Temperature 220-260
Rear-Zone 1 Temperature 200-230
Hopper Temperature 60-80
Mold Temperature 50-70
Source GMD,last updated:2012/07/30
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
PC/ABS合金塑料报价网:http://www.pa66-suliao.com/product/gcsuliao/PC/ABS/