Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin MC5215 数据
CYCOLOY MC5215 is a 15% glass reinforced PC+ABS blend for injection molding purposes, featuring of balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems.

Property
TYPICAL PROPERTIES (1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,brk,Type I,5mm/min	870	kgf/cm²	ASTM D 638
Tensile Strain,brk,Type I,5mm/min	2.7	%	ASTM D 638
Tensile Modulus,5mm/min	58800	kgf/cm²	ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span	1370	kgf/cm²	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	52500	kgf/cm²	ASTM D 790
Tensile Stress,break,5mm/min	86	MPa	ISO 527
Tensile Strain,break,5mm/min	2.5	%	ISO 527
Tensile Modulus,1mm/min	5910	MPa	ISO 527
Flexural Stress,yield,2mm/min	134	MPa	ISO 178
Flexural Modulus,2mm/min	4970	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact,notched,23℃	7	cm-kgf/cm	ASTM D 256
Izod Impact,unnotched 80*10*3 +23℃	32	kJ/m²	ISO 180/1U
Izod Impact,unnotched 80*10*3 -30℃	7	kJ/m²	ISO 180/1U
THERMAL	Value	Unit	Standard
HDT,0.45 MPa,3.2mm,unannealed	95	℃	ASTM D 648
Vicat Softening Temp,Rate B/120	100	℃	ISO 306
PHYSICAL	Value	Unit	Standard
Density	1.29	g/cm³	ASTM D 792
Melt Flow Rate,260℃/2.16 kgf	20	g/10 min	ASTM D 1238
Water Absorption,(23℃/sat)	0.15	%	ISO 62
Melt Volume Rate,MVR at 260℃/2.16 kg	17	cm³/10 min	ISO 1133
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized,94V-1 Flame Class Rating(3)	1.5	mm	UL 94
Source GMD,last updated:2012/08/30

Parameter Injection Molding	Value	Unit
Drying Temperature	80-90	℃
Drying Time	3-4	hrs
Maximum Moisture Content	0.01	%
Melt Temperature	250-280	℃
Nozzle Temperature	250-280	℃
Front-Zone 3 Temperature	250-280	℃
Middle-Zone 2 Temperature	240-280	℃
Rear-Zone 1 Temperature	230-270	℃
Mold Temperature	80-100	℃
Back Pressure	3-9	MPa
Screw Speed	30-150	rpm
Source GMD,last updated:2012/08/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.