PC/ABS XCM851 高耐热,高弹性模量,低热膨胀系数
  • 产 品:PC/ABS XCM851 高耐热,高弹性模量,低热膨胀系数
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin XCM851 数据
High heat PC/ABS blend offering high modulus / low CTE and good practical impact

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 610 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 350 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 4 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 12 % ASTM D 638
Tensile Modulus,5mm/min 48400 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1100 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 46300 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 55 MPa ISO 527
Tensile Stress,break,5mm/min 45 MPa ISO 527
Tensile Strain,yield,5mm/min 4 % ISO 527
Tensile Strain,break,5mm/min 10 % ISO 527
Tensile Modulus,1mm/min 4600 MPa ISO 527
Flexural Stress,yield,2mm/min 100 MPa ISO 178
Flexural Modulus,2mm/min 4400 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 10 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 8 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 611 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*3 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*3 +23℃ 12 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 9 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 15 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 138 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 119 ASTM D 648
CTE,-40℃ to 40℃,flow 4.10E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 5.60E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 4.10E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 5.60E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 139 ISO 306
Vicat Softening Temp,Rate B/120 140 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 122 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.3 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.3-0.5 % SABIC Method
Melt Flow Rate,260℃/5.0 kgf 12 g/10 min ASTM D 1238
Density 1.3 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.2 % ISO 62
Moisture Absorption(23℃/50% RH) 0.01 % ISO 62
Melt Volume Rate,MVR at 260℃/5.0 kg 9 cm³/10 min ISO 1133
Source GMD,last updated:2008/10/22
Parameter Injection Molding Value Unit
Drying Temperature 120-110
Drying Time 2-6 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 270-300
Nozzle Temperature 260-290
Front-Zone 3 Temperature 270-300
Middle-Zone 2 Temperature 265-290
Rear-Zone 1 Temperature 260-270
Mold Temperature 60-100
Back Pressure 0.3-0.7 MPa
Screw Speed 40-70 rpm
Shot to Cylinder Size 30-80 %
Vent Depth 0.038-0.076 mm
Parameter Sheet Extrusion Value Unit
Drying Temperature 120-120
Drying Time 2-6 hrs
Drying Time(Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-270
Barrel-Zone 1 Temperature 195-205
Barrel-Zone 2 Temperature 200-220
Barrel-Zone 3 Temperature 220-240
Barrel-Zone 4 Temperature 230-260
Adapter Temperature 230-260
Die Temperature 230-245
Roll Stack Temp-Top 100-110
Roll Stack Temp-Middle 110-120
Roll Stack Temp-Bottom 145-155
Source GMD,last updated:2008/10/22
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.