- 产 品:POM FG100TL NC010 高粘,含1.5%PTFE微粉,食品级
- 产 地:DuPont 杜邦
- 价 格:电话报价
- 库 存:20吨
- 交 货:江苏苏州
- 苏州希普能:185 5121 3137 谭经理
DuPont™ Delrin® 数据
杜邦™塑钢®
acetal resin
缩醛树脂
Extrusion Resins
挤出树脂
Delrin® 100TL is a high viscosity acetal homopolymer, containing 1.5% Teflon® PTFE Micropowder. It has been developed for consideration into applications such as parts for the food industry.
塑钢®100tl是高粘度聚甲醛均聚物,含有1.5%特富龙®PTFE微粉。它已经发展到应用食品工业等零件。
Property
|
Test Method
|
Units
|
Value
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
POM-SD
>POM-SD<
|
Mechanical
Yield Stress
Yield Strain
Nominal Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
71 (10.3)
25
33
3000 (435)
2800 (405)
8
9
150
|
Property
|
Test Method
|
Units
|
Value
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
|
158 (315)
95 (205)
178 (352)
1.0 (0.57)
1.1 (0.61)
1.5 (0.84)
1.0 (0.56)
1.1 (0.61)
1.6 (0.88)
|
Rheological
Melt Mass-Flow Rate
190°C, 2.16kg
|
ISO 1133
|
g/10 min
|
2.2
|
Other
Density
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m (g/cm )
%
|
1430 (1.43)
1.7
1.8
|
Processing - Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Range
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
MPa (kpsi)
|
210-220 (410-430)
215 (420)
80-100 (175-210)
90 (195)
2-4
80 (175)
<0.2
90-110 (13-16)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc Test specimen for ISO 527 is 1BA (2mm) at 50mm/min; all other ISO & ASTM mechanical properties measured at 4mm; ISO electrical properties measured at 2mm All mechanical & electrical properties measured on injection molded specimen
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2011