快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：POM 500CL NC010 中粘,润滑剂,低摩擦磨耗
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
DuPont™ Delrin® 数据
杜邦™塑钢®
acetal resin
缩醛树脂
Low Wear and Friction Resins
低摩擦磨耗
Delrin® 500CL is a medium viscosity acetal homopolymer resin containing a chemical lubricant, designed for low wear and friction against metals.
塑钢®500cl是一个中等粘度聚甲醛均聚物树脂含有化学润滑油，低磨损和对金属的摩擦而设计的。
|
Property
|
Test Method
|
Units
|
Value
|
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
POM
>POM<
|
|
Mechanical
Yield Stress
Yield Strain
Strain at Break
50mm/min
Nominal Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
%
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
67 (9.7)
15
45
25
3100 (450)
2900 (420)
8
9
290
350
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Parallel
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
|
158 (315)
90 (194)
178 (352)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Thermal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
Vicat Softening Temperature
50N
|
ISO 11359-1/-2
ISO 306
|
E-4/C (E-4/F)
°C (°F)
|
0.92 (0.51)
1.11 (0.61)
1.6 (0.89)
1.0 (0.56)
1.1 (0.63)
1.7 (0.94)
159 (318)
|
|
Rheological
Melt Mass-Flow Rate
190°C, 2.16kg
|
ISO 1133
|
g/10 min
|
15
|
|
Electrical
Surface Resistivity
Relative Permittivity
1E6 Hz
Dissipation Factor
1E6 Hz
CTI
|
IEC 60093
IEC 60250
IEC 60250
IEC 60112
|
ohm
E-4
V
|
>1E15
3.5
60
600
|
|
Flammability
Flammability Classification
0.75mm
1.5mm
3.0mm
Oxygen Index
|
IEC 60695-11-10
ISO 4589-1/-2
|
%
|
HB
HB
HB
22
|
|
Temperature Index
RTI, Electrical
0.75mm
1.5mm
3.0mm
|
UL 746B
|
°C
|
50
100
100
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Temperature Index
RTI, Impact
0.75mm
1.5mm
3.0mm
RTI, Strength
0.75mm
1.5mm
3.0mm
|
UL 746B
UL 746B
|
°C
°C
|
50
80
80
50
85
85
|
|
Other
Density
Hardness, Rockwell
Scale M
Scale R
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1410 (1.41)
92
120
0.25
1
1.8
1.9
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Range
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
MPa (kpsi)
|
210-220 (410-430)
215 (420)
80-100 (175-210)
90 (195)
2-4
80 (175)
<0.2
80-100 (12-15)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™,The miracles of science™ and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2006.