DuPont™ Delrin® 数据
杜邦™塑钢®
acetal resin
缩醛树脂
Low Wear and Friction Resins
低摩擦磨耗
Delrin® 300ATB BK000 is a filled, medium viscosity, toughened acetal homopolymer for injection molding. It is well suited for antistatic applications.
塑钢®300atb bk000是一个填充,中等粘度,增韧的聚缩醛射出成型。它非常适合抗静电应用。
Property
|
Test Method
|
Units
|
Value
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
|
50 (7.3)
16
2300 (334)
2100 (300)
8
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
°C (°F)
°C (°F)
|
135 (275)
70 (158)
178 (352)
|
Rheological
Melt Mass-Flow Rate
190°C, 2.16kg
|
ISO 1133
|
g/10 min
|
2.3
|
Electrical
Surface Resistivity
Volume Resistivity
|
IEC 60093
IEC 60093
|
ohm
ohm m
|
1E05
1E3
|
Property
|
Test Method
|
Units
|
Value
|
Other
Density
Mold Shrinkage
Normal, 4mm ISO bar
Parallel, 4mm ISO bar
|
ISO 1183
|
3 3
kg/m (g/cm )
%
|
1410 (1.41)
1.5
1.7
|
Processing - Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Range
Hold Pressure Time
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
MPa (kpsi)
s/mm (s/in)
|
200-210 (390-410)
205 (400)
80-100 (175-210)
90 (195)
2-4
80 (175)
<0.05
80-100 (12-15)
7-9 (175-225)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The above data are preliminary and are subject to change as additional data are developed on subsequent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2008