POM FG500P NC010 中高粘,热稳定,食品级
  • 产 品:POM FG500P NC010 中高粘,热稳定,食品级
  • 产 地:DuPont 杜邦
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

DuPont™ Delrin® 数据
杜邦™塑钢®
acetal resin
缩醛树脂
Unreinforced Resins
增强树脂

Delrin® FG500P is a medium viscosity acetal homopolymer, with improved thermal stability. It has been developed for consideration into applications such as parts for the food industry.
塑钢®fg500p是中高粘度聚甲醛均聚物,具有改善的热稳定性。它已制定考虑到应用等食品工业的零件。

Property
Test Method
Units
Value
Identification
Resin Identification
Part Marking Code
ISO 1043
ISO 11469
 
POM
>POM<
Mechanical
Yield Stress
Yield Strain
Nominal Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Flexural Modulus
Notched Charpy Impact Strength
-40°C (-40°F)
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
ISO 527
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 179/1eA
ISO 179/1eU
MPa (kpsi)
%
%
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
70 (10.1)
17
30
3100 (450)
2800 (406)
1600 (232)
2900 (420)
8
8
9
240
300

Property
Test Method
Units
Value
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
158 (316)
94 (201)
178 (352)
1.0 (0.56)
1.1 (0.61)
1.5 (0.82)
1.0 (0.56)
1.1 (0.61)
1.6 (0.9)
Rheological
Melt Mass-Flow Rate
190°C, 2.16kg
Melt Volume-Flow Rate
ISO 1133
ISO 1133
g/10 min
3
cm /10 min (ml/10 min)
15
13
Other
Density
Water Absorption
Equilibrium 50%RH
Immersion 24h
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
ISO 1183
ISO 62, Similar to
ISO 294-4
3           3
kg/m (g/cm )
%
%
1420 (1.42)
0.3
0.6
1.4
1.9
2.0

Property
Test Method
Units
Value
Processing - Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Range
 
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
MPa (kpsi)
210-220 (410-430)
215 (420)
80-100 (175-210)
90 (195)
2-4
80 (175)
<0.2
80-100 (12-15)

Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.

The above data are preliminary and are subject to change as additional data are developed on subsequent lots.

The DuPont Oval Logo, DuPont™, The miracles of science™ and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2010