- 产 品:POM 570 NC000 GF20,高粘,高刚,低翘曲,抗蠕变
- 产 地:DuPont 杜邦
- 价 格:电话报价
- 库 存:20吨
- 交 货:江苏苏州
- 苏州希普能:185 5121 3137 谭经理
DuPont™ Delrin® 数据
杜邦™塑钢®
acetal resin
缩醛树脂
Glass or Mineral Filled Resins
玻璃或矿物填充树脂
Delrin® 570 NC000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler for injection molding. Delrin® 570 has very high stiffness, low warpage, and good creep resistance.
塑钢®570nc000是中高粘度聚甲醛均聚物含20%玻璃纤维填充注射成型。塑钢®570具有很高的刚度,低翘曲,和良好的抗蠕变。
Property
|
Test Method
|
Units
|
Value
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
POM-GF20
>POM-GF20<
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
53 (7.7)
12
5000 (725)
4600 (667)
3
3.5
50
54
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
°C (°F)
°C (°F)
|
163 (325)
122 (252)
178 (352)
|
Rheological
Melt Volume-Flow Rate
|
ISO 1133
|
3
cm /10 min (ml/10 min)
|
7
|
Property
|
Test Method
|
Units
|
Value
|
Electrical
Surface Resistivity
Volume Resistivity
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E6 Hz
|
IEC 60093
IEC 60093
IEC 60250
IEC 60250
|
ohm
ohm m
E-4
|
>1E15
1E13
3.9
3.9
50
|
Flammability
Flammability Classification
1.5mm
Flammability Classification
1.5mm
|
IEC 60695-11-10
UL94
|
|
HB
HB
|
Temperature Index
RTI, Electrical
1.5mm
3.0mm
RTI, Impact
1.5mm
3.0mm
RTI, Strength
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
105
105
85
85
90
90
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1560 (1.56)
0.1
0.8
1.2
1.6
|
Property
|
Test Method
|
Units
|
Value
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Hold Pressure Range
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
MPa (kpsi)
|
210-220 (410-430)
215 (420)
80-100 (175-210)
90 (195)
2-4
80 (175)
80-100 (12-15)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The above data are preliminary and are subject to change as additional data are developed on subsequent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2008