LNP STAT-KON* ACETAL COMPOUND
ADD TAILORED ELECTRICAL PROPERTIES TO ACETALS
Acetal-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound POM KX02764 塑料数据物性表

Also known as:LNP™ Stat-kon™ Compound PDX-K-02764
Product reorder name:KX02764
LNP STAT-KON* KX02764 is a compound based on Acetal resin containing Carbon Powder. Added features of this material include: Electrically Conductive.

MECHANICAL Value Unit Standard
Tensile Stress,yield 540 kgf/cm² ASTM D 638
Tensile Stress,break 480 kgf/cm² ASTM D 638
Tensile Strain,yield 3.8 % ASTM D 638
Tensile Strain,break 10.2 % ASTM D 638
Tensile Modulus,50mm/min 35500 kgf/cm² ASTM D 638
Flexural Stress 1020 kgf/cm² ASTM D 790
Flexural Modulus 30700 kgf/cm² ASTM D 790
Tensile Stress,yield 53 MPa ISO 527
Tensile Stress,break 46 MPa ISO 527
Tensile Strain,yield 4 % ISO 527
Tensile Strain,break 18.1 % ISO 527
Tensile Modulus,1mm/min 3460 MPa ISO 527
Flexural Stress 96 MPa ISO 178
Flexural Modulus 3010 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 38 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 31 cm-kgf ASTM D 3763
Multiaxial Impact 77 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 52 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 106 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 103 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.443 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.18 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 1.5-3.5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1.5-3.5 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 1.5-3.5 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 1.5-3.5 % ISO 294
Density 1.43 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.25 % ISO 62
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+02-1.E+06 Ohm-cm ASTM D 257
Surface Resistivity 1.E+02-1.E+06 Ohm ASTM D 257
Source GMD,last updated:2004/10/01
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Melt Temperature 200-215
Front-Zone 3 Temperature 210-220
Middle-Zone 2 Temperature 195-205
Rear-Zone 1 Temperature 175-190
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/10/01

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ STAT-KON™ Compound POM KX02764