PPS OCL36 含炭纤维和聚四氟乙烯,导电级
  • 产 品:PPS OCL36 含炭纤维和聚四氟乙烯,导电级
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP Lubricomp* High Temperature Resins Compound
Adding friction control & wear resistance
High temperature LNP Lubricomp compounds provide Improved wear resistance and lower friction by combining internal lubricants with high performance base resins. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound PPS OCL36 塑料物性

Also known as:LNP™ Lubricomp™ Compound OCL-4036
Product reorder name:OCL36
LNP LUBRICOMP* OCL36 is a compound based on PPS - Linear resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.

MECHANICAL Value Unit Standard
Tensile Stress,break 1720 kgf/cm² ASTM D 638
Tensile Strain,break 1.4 % ASTM D 638
Tensile Modulus,50mm/min 219400 kgf/cm² ASTM D 638
Flexural Stress 2640 kgf/cm² ASTM D 790
Flexural Modulus 215300 kgf/cm² ASTM D 790
Tensile Stress,break 167 MPa ISO 527
Tensile Strain,break 1.1 % ISO 527
Tensile Modulus,1mm/min 30680 MPa ISO 527
Flexural Stress 262 MPa ISO 178
Flexural Modulus 21110 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 45 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 5 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 153 cm-kgf ASTM D 3763
Multiaxial Impact 30 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 31 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 6 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 267 ASTM D 648
CTE,-40℃ to 40℃,flow 1.62E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 3.42E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 1.76E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 3.44E-05 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 263 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.52 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.04-0.1 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.3-0.4 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.04-0.1 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.36-0.4 % ISO 294
Wear Factor Washer 19 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.39 - ASTM D 3702 Modified
Static COF 0.34 - ASTM D 3702 Modified
Density 1.52 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.03 % ISO 62
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 1.8 mm UL 94 by SABIC-IP
Source GMD,last updated:2004/09/29
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Melt Temperature 315-320
Front-Zone 3 Temperature 330-345
Middle-Zone 2 Temperature 320-330
Rear-Zone 1 Temperature 305-315
Mold Temperature 140-165
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/09/29

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.