PPS OL003A 含玻璃纤维,聚四氟乙烯,内部润滑
  • 产 品:PPS OL003A 含玻璃纤维,聚四氟乙烯,内部润滑
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ Lubricomp™ Compound PPS OL003A 塑料数据

LNP* Lubricomp* OL003A is a compound based on Branched PPS containing PTFE. Characteristics of this grade are: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 210 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 0.6 % ASTM D 638
Tensile Modulus,50mm/min 36600 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 660 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 39400 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 20 MPa ISO 527
Tensile Strain,break,5mm/min 0.6 % ISO 527
Tensile Modulus,1mm/min 3360 MPa ISO 527
Flexural Stress 56 MPa ISO 178
Flexural Modulus,2mm/min 3320 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 7 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 1 cm-kgf/cm ASTM D 256
Multiaxial Impact 4 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 10 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 4 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 2 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 175 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 108 ASTM D 648
CTE,-30℃ to 30℃,flow 6.00E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 6.60E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 178 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 109 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.44 - ASTM D 792
Density 1.43 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.02 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.9-2 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1-3 % ASTM D 955
Moisture Absorption(23℃/50% RH) 0.04 % ISO 62
Source GMD,last updated:2010/04/20
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Melt Temperature 315-320
Front-Zone 3 Temperature 330-345
Middle-Zone 2 Temperature 320-330
Rear-Zone 1 Temperature 305-315
Mold Temperature 140-165
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2010/04/20

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.