PPS OE006A 含有碳纤维.导电PPS
  • 产 品:PPS OE006A 含有碳纤维.导电PPS
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP STAT-KON* HIGH TEMPERATURE RESINS COMPOUND
BALANCE HIGH TEMPERATURE AND ELECTRICAL PROPERTIES
High temperature LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound PPS OE006A 塑料数据物性表

Also known as:LNP™ Stat-kon™ Compound OC-1006
Product reorder name:OE006A
LNP STAT-KON* OE006A is a compound based on PPS - Branched resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.

MECHANICAL Value Unit Standard
Tensile Stress,break 2140 kgf/cm² ASTM D 638
Tensile Strain,break 1.1 % ASTM D 638
Tensile Modulus,50mm/min 333900 kgf/cm² ASTM D 638
Flexural Stress 3100 kgf/cm² ASTM D 790
Flexural Modulus 239700 kgf/cm² ASTM D 790
Tensile Stress,break 204 MPa ISO 527
Tensile Strain,break 1 % ISO 527
Tensile Modulus,1mm/min 25450 MPa ISO 527
Flexural Stress 311 MPa ISO 178
Flexural Modulus 24720 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 44 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 5 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 33 cm-kgf ASTM D 3763
Multiaxial Impact 17 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 28 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
CTE,-40℃ to 40℃,flow 7.20E-06 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 3.96E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 8.70E-06 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 4.08E-05 1/℃ ISO 11359-2
PHYSICAL Value Unit Standard
Density 1.44 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.02 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.1 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.4 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.08 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.4 % ISO 294
Wear Factor Washer 857 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 1.6 - ASTM D 3702 Modified
Static COF 1.38 - ASTM D 3702 Modified
Density 1.44 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.03 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+02-1.E+06 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 1 mm UL 94 by SABIC-IP
Source GMD,last updated:2011/06/29
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Melt Temperature 315-320
Front-Zone 3 Temperature 330-345
Middle-Zone 2 Temperature 320-330
Rear-Zone 1 Temperature 305-315
Mold Temperature 140-165
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2011/06/29

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.