快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PPS OEP32 含炭纤维,聚四氟乙烯,硅酮.导电PPS
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP STAT-KON* HIGH TEMPERATURE RESINS COMPOUND
BALANCE HIGH TEMPERATURE AND ELECTRICAL PROPERTIES
High temperature LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PPS OEP32 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound OCL-4532 LEX
Product reorder name:OEP32
LNP STAT-KON* OEP32 is a compound based on PPS - Linear resin containing Carbon Fiber, PTFE, Silicone. Added features of this material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,break | 1300 | kgf/cm² | ASTM D 638 |
| Tensile Strain,break | 1.6 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 107700 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 1960 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 87100 | kgf/cm² | ASTM D 790 |
| Tensile Stress,break | 125 | MPa | ISO 527 |
| Tensile Strain,break | 2 | % | ISO 527 |
| Tensile Modulus,1mm/min | 10590 | MPa | ISO 527 |
| Flexural Stress | 431 | MPa | ISO 178 |
| Flexural Modulus | 27090 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 43 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 3 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 85 | cm-kgf | ASTM D 3763 |
| Multiaxial Impact | 25 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | 23 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.41 | g/cm³ | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 0.5-0.7 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.6-0.8 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 0.5-0.7 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.6-0.8 | % | ISO 294 |
| Wear Factor Washer | 39 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.32 | - | ASTM D 3702 Modified |
| Static COF | 0.33 | - | ASTM D 3702 Modified |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Moisture Absorption(23℃/50% RH) | 0 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02-1.E+04 | Ohm | ASTM D 257 |
| Source GMD,last updated:2005/04/26 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120-150 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 315-320 | ℃ |
| Front-Zone 3 Temperature | 330-345 | ℃ |
| Middle-Zone 2 Temperature | 320-330 | ℃ |
| Rear-Zone 1 Temperature | 305-315 | ℃ |
| Mold Temperature | 140-165 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2005/04/26 | ||