快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PPS OEL36A 含聚四氟乙烯,碳纤维.导电聚苯硫醚树脂
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP™ STAT-KON™ Compound PPS OEL36A 塑料物性表
Also known as:LNP™ Stat-kon™ Compound OCL-4036 Product reorder name:OEL36A
LNP* Stat-Kon* OEL36A is a compound based on Polyphenylene Sulfide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 1730 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 1750 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 0.9 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 271400 | kgf/cm² | ASTM D 638 |
| Flexural Stress,brk,1.3mm/min,50mm span | 2290 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 211000 | kgf/cm² | ASTM D 790 |
| Tensile Stress,break,5mm/min | 168 | MPa | ISO 527 |
| Tensile Strain,break,5mm/min | 0.9 | % | ISO 527 |
| Tensile Modulus,1mm/min | 25160 | MPa | ISO 527 |
| Flexural Stress | 258 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 21620 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 40 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 4 | cm-kgf/cm | ASTM D 256 |
| Multiaxial Impact | 20 | cm-kgf | ISO 6603 |
| Instrumented Impact Total Energy,23℃ | 54 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | 22 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 277 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 263 | ℃ | ASTM D 648 |
| CTE,-30℃ to 30℃,flow | 8.20E-06 | 1/℃ | ASTM D 696 |
| CTE,-30℃ to 30℃,xflow | 4.13E-05 | 1/℃ | ASTM D 696 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 277 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 262 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.54 | - | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.02 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.05-0.07 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.5-0.7 | % | ASTM D 955 |
| Density | 1.54 | g/cm³ | ISO 1183 |
| Moisture Absorption(23℃/50% RH) | 0.03 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+00-3.E+00 | Ohm | ASTM D 257 |
| Source GMD,last updated:2009/08/27 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120-150 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 315-320 | ℃ |
| Front-Zone 3 Temperature | 330-345 | ℃ |
| Middle-Zone 2 Temperature | 320-330 | ℃ |
| Rear-Zone 1 Temperature | 305-315 | ℃ |
| Mold Temperature | 140-165 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2009/08/27 | ||