快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：TPU DP 1485A 挤出和注塑级
- 产 地：Bayer 拜耳
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Datasheet Desmopan DP 1485A 数据
Extrusion- and injection molding grade; suitable for extrusion blow molding; Application; Bellows; Hoses, non-reinforced; Profiles; Injection molded engineering parts
☆These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break
| ISO Shortname: | |||||||
| Property | Test Condition | Unit | Standard | Value | |||
| . | drying according to specifications annealed - | ||||||
| Mechanical properties(23℃/50 % r. h.) | |||||||
| ☆ | shore hardness, method A | . | - | ISO 868 | . | 86 | . |
| ☆ | shore hardness, method D | . | - | ISO 868 | . | 33 | . |
| . | Ultimate tensile strength | 200 mm/min | MPa | DIN 53504 | . | 46 | . |
| . | Strain at break | 200 mm/min | % | DIN 53504 | . | 630 | . |
| . | Stress at 100 % strain | 200 mm/min | MPa | DIN 53504 | . | 5 | . |
| . | Stress at 300 % strain | 200 mm/min | MPa | DIN 53504 | . | 9 | . |
| ☆ | Compression set | 24 h; 70℃ | % | ISO 815 | . | 36 | . |
| ☆ | Compression set | 72 h; 23℃ | % | ISO 815 | . | 11 | . |
| ☆ | Abrasion resistance | . | mm³ | ISO 4649 | . | 19 | . |
| . | Impact resilience | . | % | ISO 4662 | . | 46 | . |
| . | Tear propagation resistance | 500 mm/min | kN/m | ISO 34-1 | . | 78 | . |
| Thermal properties | |||||||
| . | Torsional storage modulus | -20℃ | MPa | ISO 6721-2 | . | 63 | . |
| . | Torsional storage modulus | 23℃ | MPa | ISO 6721-2 | . | 10 | . |
| . | Torsional storage modulus | 70℃ | MPa | ISO 6721-2 | . | 7 | . |
| . | Tensile storage modulus | -20℃ | MPa | ISO 6721-1,-4 | . | 390 | . |
| . | Tensile storage modulus | 20℃ | MPa | ISO 6721-1,-4 | . | 44 | . |
| . | Tensile storage modulus | 60℃ | MPa | ISO 6721-1,-4 | . | 32 | . |
| Other properties(23℃) | |||||||
| ☆ | Density | . | kg/m³ | ISO 1183-1 | . | . | 1216 |
| Molding conditions | |||||||
| . | Injection molding-Melt temperature | . | ℃ | - | 200-220 | . | . |
| . | Injection molding-Mold temperature | . | ℃ | - | . | . | 20 |
| . | Extrusion-Melt temperature | . | ℃ | - | 180-200 | . | . |
| . | Maximum drying temperature | . | ℃ | - | . | . | 80 |