Datasheet Desmopan DP 2384A 数据
Extrusion grade; does not contain any anti-hydrolysis agent; food contact applications are possible, contact our HSEQ department; Application; Films; Hoses, non-reinforced
☆These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break
ISO Shortname: | |||||||
Property | Test Condition | Unit | Standard | Value | |||
. | drying according to specifications annealed - | ||||||
Mechanical properties(23℃/50 % r. h.) | |||||||
☆ | shore hardness, method A | . | - | ISO 868 | . | 83 | . |
. | Ultimate tensile strength | 200 mm/min | MPa | DIN 53504 | . | 44 | . |
. | Strain at break | 200 mm/min | % | DIN 53504 | . | 681 | . |
. | Stress at 10 % strain | 200 mm/min | MPa | DIN 53504 | . | 1,6 | . |
. | Stress at 50 % strain | 200 mm/min | MPa | DIN 53504 | . | 4,3 | . |
. | Stress at 100 % strain | 200 mm/min | MPa | DIN 53504 | . | 5,5 | . |
. | Stress at 300 % strain | 200 mm/min | MPa | DIN 53504 | . | 10,4 | . |
Thermal properties | |||||||
. | Tensile storage modulus | -20℃ | MPa | ISO 6721-1,-4 | . | 443 | . |
. | Tensile storage modulus | 20℃ | MPa | ISO 6721-1,-4 | . | 26 | . |
. | Tensile storage modulus | 60℃ | MPa | ISO 6721-1,-4 | . | 12 | . |
Molding conditions | |||||||
. | Injection molding-Melt temperature | . | ℃ | - | 190-210 | . | . |
. | Injection molding-Mold temperature | . | ℃ | - | . | . | 20-40 |
. | Extrusion-Melt temperature | . | ℃ | - | 190-210 | . | . |