- 产 品：PP MS000IL 含不锈钢.导电级聚丙烯,食品级聚丙烯
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ STAT-KON™ Compound PP MS000IL 塑料物性表
Also known as:LNP™ Stat-kon™ Compound MS-HI LE Product reorder name:MS000IL
LNP* Stat-kon* MS000IL is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: High Impact, Low Extractible, Electrically Conductive, food contact compliant raw materials and metal detectable.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 210 | kgf/cm² | ASTM D 638 |
| Tensile Stress,break | 150 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yield | 7.1 | % | ASTM D 638 |
| Tensile Strain,break | 76 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 12800 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 280 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 13000 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield | 20 | MPa | ISO 527 |
| Tensile Stress,break | 16 | MPa | ISO 527 |
| Tensile Strain,yield | 5.6 | % | ISO 527 |
| Tensile Strain,break | 38.9 | % | ISO 527 |
| Tensile Modulus,1mm/min | 1170 | MPa | ISO 527 |
| Flexural Stress | 24 | MPa | ISO 178 |
| Flexural Modulus | 1180 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 135 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 9 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 111 | cm-kgf | ASTM D 3763 |
| Multiaxial Impact | 101 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | NB | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 52 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 9.90E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 1.17E-04 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 1.01E-04 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 1.17E-04 | 1/℃ | ISO 11359-2 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 52 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 0.96 | g/cm³ | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 1.3 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.4 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 1.29 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.38 | % | ISO 294 |
| Density | 0.96 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Source GMD,last updated:2011/04/19 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 225-250 | ℃ |
| Front-Zone 3 Temperature | 240-250 | ℃ |
| Middle-Zone 2 Temperature | 215-225 | ℃ |
| Rear-Zone 1 Temperature | 195-205 | ℃ |
| Mold Temperature | 30-50 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2011/04/19 | ||