ABS AX03654 阻燃级
  • 产 品:ABS AX03654 阻燃级
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP Colorcomp* Styrenics Compound
High performance custom color
Styrenic LNP Colorcomp pre-colored unfilled compounds offer a broad portfolio of colorants and special effects to create a dazzling spectrum of colored materials. Offerings include opaque, translucent, and transparent resins, plus special effects, including edge glow, sparkle, glow, pearlescent, and thermochromic.

LNP™Colorcomp™ Compound ABS AX03654 数据

Also known as:LNP™Colorcomp™Compound PDX-A-03654
Product reorder name:AX03654
LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.

MECHANICAL Value Unit Standard
Tensile Stress,yield 400 kgf/cm² ASTM D 638
Tensile Stress,break 310 kgf/cm² ASTM D 638
Tensile Strain,yield 2.1 % ASTM D 638
Tensile Strain,break 13.6 % ASTM D 638
Tensile Modulus,50mm/min 24900 kgf/cm² ASTM D 638
Flexural Stress 660 kgf/cm² ASTM D 790
Flexural Modulus 24300 kgf/cm² ASTM D 790
Tensile Stress,yield 38 MPa ISO 527
Tensile Stress,break 31 MPa ISO 527
Tensile Strain,yield 2 % ISO 527
Tensile Strain,break 15.3 % ISO 527
Tensile Modulus,1mm/min 2390 MPa ISO 527
Flexural Stress 65 MPa ISO 178
Flexural Modulus 2310 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 108 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 17 cm-kgf/cm ASTM D 256
Izod Impact,unnotched 80*10*4 +23℃ 39 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 11 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 72 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 72 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.16 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.5-0.7 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.5-0.7 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.5-0.7 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.5-0.7 % ISO 294
Density 1.16 g/cm³ ISO 1183
Source GMD,last updated:2004/10/05
Parameter Injection Molding Value Unit
Drying Temperature 70-80
Drying Time 4 hrs
Maximum Moisture Content 0.05-0.1 %
Melt Temperature 200-210
Front-Zone 3 Temperature 205-215
Middle-Zone 2 Temperature 195-205
Rear-Zone 1 Temperature 180-195
Mold Temperature 10-50
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/10/05

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.HDPE 7501 中空吹制级
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™Colorcomp™ Compound ABS AX03654