LNP* Colorcomp* Compound
LNP Colorcomp All Series
LNP* Colorcomp* resins contain colorants and special effects for a dazzling spectrum of colored materials. Among the offerings are opaque, translucent, and transparent resins, plus special effects, including edge glow, sparkle, glow, pearlescent, and thermochromic. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™Colorcomp™ Compound ABS A1000H 数据
Also known as:LNP™Colorcomp™Compound A-1000 EES HC
Product reorder name:A1000H
LNP* Colorcomp* A1000HC is an unfilled compound based on ABS. Characteristics of this grade are Healthcare.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 440 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 340 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 2 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 24 % ASTM D 638
Tensile Modulus,5mm/min 23200 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 730 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 23900 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 50 MPa ISO 527
Tensile Stress,break,5mm/min 35 MPa ISO 527
Tensile Strain,yield,5mm/min 2.6 % ISO 527
Tensile Strain,break,5mm/min 24.8 % ISO 527
Tensile Modulus,1mm/min 2530 MPa ISO 527
Flexural Stress,yield,2mm/min 76 MPa ISO 178
Flexural Modulus,2mm/min 2410 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 32 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 13 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 315 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*4 +23℃ 23 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 8 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 18 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 98 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 94 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 80 ASTM D 648
CTE,-40℃ to 40℃,flow 8.82E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.82E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 8.82E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 8.82E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 100 ISO 306
Vicat Softening Temp,Rate B/120 100 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 80 ISO 75/Af
Relative Temp Index,Elec 60 UL 746B
Relative Temp Index,Mech w/impact 60 UL 746B
Relative Temp Index,Mech w/o impact 60 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.05 - ASTM D 792
Melt Flow Rate,230℃/3.8 kgf 5.6 g/10 min ASTM D 1238
Melt Viscosity,240℃,1000 sec-1 2300 poise ASTM D 3825
Density 1.05 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 1 % ISO 62
Moisture Absorption(23℃/50% RH) 0.2 % ISO 62
Melt Flow Rate,220℃/10.0 kg 19 g/10 min ISO 1133
Melt Volume Rate,MVR at 220℃/5.0 kg 14 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Arc Resistance,Tungsten{PLC} 6 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 3 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 3 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94HB Flame Class Rating(3) 1.52 mm UL 94
Source GMD,last updated:2010/06/29
Parameter Injection Molding Value Unit
Drying Temperature 80-95
Drying Time 2-4 hrs
Drying Time(Cumulative) 8 hrs
Maximum Moisture Content 0.1 %
Melt Temperature 220-260
Nozzle Temperature 220-260
Front-Zone 3 Temperature 215-240
Middle-Zone 2 Temperature 205-225
Rear-Zone 1 Temperature 190-210
Mold Temperature 50-70
Back Pressure 0.3-0.7 MPa
Screw Speed 30-60 rpm
Shot to Cylinder Size 50-70 %
Vent Depth 0.038-0.051 mm
Source GMD,last updated:2010/06/29

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.TPU DP 3695AU 水解稳定,抗紫外线,易脱模和耐磨
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™Colorcomp™ Compound ABS A1000H