- 产 品：ABS AS003 导电,EMI/RFI屏蔽,含有不锈钢
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP Faradex* Styrenics Compound
Electromagnetic, RFI attenuation for cost-effectiv
Styrenic LNP Faradex compounds provide electromagnetic and radio frequency interference (EMI/RFI) attenuation for a broad range of cost-effective resins.
LNP™Faradex™ Compound ABS AS003 数据
Also known as:LNP™Faradex™Compound AS-1003
Product reorder name:AS003
LNP* Faradex* AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 420 | kgf/cm² | ASTM D 638 |
| Tensile Stress,break | 400 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yield | 2.6 | % | ASTM D 638 |
| Tensile Strain,break | 6.2 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 32200 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 770 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 31000 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield | 38 | MPa | ISO 527 |
| Tensile Stress,break | 37 | MPa | ISO 527 |
| Tensile Strain,yield | 2.2 | % | ISO 527 |
| Tensile Strain,break | 2.8 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2700 | MPa | ISO 527 |
| Flexural Stress | 66 | MPa | ISO 178 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 31 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 152 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | 18 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 96 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 88 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 7.74E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 6.30E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 7.10E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 9.30E-05 | 1/℃ | ISO 11359-2 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 93 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 78 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.16 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.2 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.3 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.4 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 0.27 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.39 | % | ISO 294 |
| Density | 1.15 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.00E+04 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+01-1.E+03 | Ohm | ASTM D 257 |
| Shielding Effectivness @ 3mm | 50-65 | dB | SABIC Method |
| Source GMD,last updated:2007/02/27 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05-0.1 | % |
| Melt Temperature | 240-255 | ℃ |
| Front-Zone 3 Temperature | 255-265 | ℃ |
| Middle-Zone 2 Temperature | 230-245 | ℃ |
| Rear-Zone 1 Temperature | 210-220 | ℃ |
| Mold Temperature | 70-95 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2007/02/27 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.塑料制品开裂、浇口区冷料斑问题分析
关健字：【LNP™Faradex™ Compound ABS AS003】